FLEX NORYL™ Resin WCD883A - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD883A resin is a flexible, non-reinforced extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting EN 50265-2-1 requirements. FLEX NORYL WCD883A resin was developed for evaluation in AC cable jacket applications such as HD 21.14 flexible cables that require EU VDE and dark color. It has a Shore A Hardness reading of 88 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Ingeniería eléctrica

Electrónica

Pantallas

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Densidad relativa	23.0 °C	1.14 [-] Show Supplier Material materials with Densidad relativa of 1.14 [-]	ASTM D 792 \|

Mecánica

Property	Temperature	Value	Comment
Dureza Shore A	23.0 °C	88 [-] Show Supplier Material materials with Dureza Shore A of 88 [-]	ASTM D 2240 \| 30S reading
Elongación	23.0 °C	220 % Show Supplier Material materials with Elongación of 220 %	ISO 527 \| break, 50 mm/min
Módulo de flexión	23.0 °C	0 GPa Show Supplier Material materials with Módulo de flexión of 0 GPa	ISO 178 \| 12.5 mm/min
Resistencia a la tracción	23.0 °C	15 MPa Show Supplier Material materials with Resistencia a la tracción of 15 MPa	ISO 527 \| break, 50 mm/min

Aplicaciones térmicas

Property	Value	Comment
Brittleness temperature	-40 °C Show Supplier Material materials with Brittleness temperature of -40 °C	<, ASTM D 746
Glow Wire Ignition Temperature	775 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 775 °C	IEC 60695-2-13 \| 3.0 mm
Inflamabilidad	Glow Wire Flammability Index 850°C, passes at: 3mm IEC 60695-2-12

Eléctrico

Property	Temperature	Value	Comment
Volume resistivity	23.0 °C	1.30E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.30E+16 Ω·cm	ASTM D 257
Índice de seguimiento comparativo	23.0 °C	600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V	IEC 60112 \|

Rheological Properties

Property	Value	Comment
Velocidad de flujo de la masa derretida	5 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5 g/10min	ASTM D 1238 \| 250°C/10.0 kgf

Technological properties

Property
Application areas	Power Manangement, Wire & cable
Availability	Asia,Americas
Processing methods	Drying Temperature: 75 to 85.0°C Drying Time: 5 to 7.0hrs Drying Time (Cumulative): 12hrs Maximum Moisture Content: 0.02% Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1- Screw Speed: 15 to 85.0rpm Feed Zone Temperature: 180 to 220.0°C Middle Zone Temperatures: 220 to 250.0°C Head Zone Temperature: 220 to 250.0°C Neck Temperature: 220 to 250.0°C Cross-head Temperature: 220 to 250.0°C Die Temperature: 220 to 250.0°C Melt Temperature: 220 to 250.0°C Conductor Pre-heat Temperature: 25 to 120.0°C Screen Pack: 150 to 100.0- Cooling Water Air Gap: 100 to 200.0mm Water Bath Temperature: 15 to 60.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.