General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Supplier Material materials with Absorción de agua of 0.2 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Densidad of 1.3 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Supplier Material materials with Elongación of 2.5 % | ISO 527 | break, 5 mm/min |
Hardness, Ball Indentation | 23.0 °C | 240 MPa Show Supplier Material materials with Hardness, Ball Indentation of 240 MPa | ISO 2039-1 | H358/30 |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 465 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 465 J/m | ASTM D 4812 | unnotched, -30°C |
Módulo de flexión | 23.0 °C | 8.1 GPa Show Supplier Material materials with Módulo de flexión of 8.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 9.6 GPa Show Supplier Material materials with Módulo elástico of 9.6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 192 MPa Show Supplier Material materials with Resistencia a la flexión of 192 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 133 MPa Show Supplier Material materials with Resistencia a la tracción of 133 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 30 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 30 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Taber Abrasion | 23.0 °C | 65 mg/1000cy Show Supplier Material materials with Taber Abrasion of 65 mg/1000cy | SABIC method | CS-17, 1 kg |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Heat deflection temperature, 1.80 MPa | 145 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 145 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |
Temperatura de flexión bajo carga | 145 - 150 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 145 - 150 °C | ||
Temperatura de reblandecimiento Vicat | 158 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 158 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción transversal of 0.2 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 9 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 9 g/10min | ASTM D 1238 | 300°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 30 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 30 cm³/10min | ISO 1133 | MVR at 300°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Vending Machine, Water Treatment/Filtration, Meter Water, Smart Water Meter, Small Appliance, Plumbing, Pipe/Fitting, Pump, Heavy Vehicles, Hot Water System, Fixture Bath/Shower, Electronic Components, Coffee Maker/Espresso Machine | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Hopper Temperature: 60 to 80.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |