NORYL™ Resin NHP9023 - Asia

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NHP9023 resin is a 15% glass reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 1.5mm and V1 at 0.75mm for thin-wall molding capability. NORYL NHP9023 is based on a unique co-polymer technology and exhibits good dimensional stability, high heat resistance, strong electrical performance, and very low specific gravity. It is an excellent candidate for copier fuser units, business equipment internal components, and electrical applications where thin-wall FR, modulus retention, and high heat resistance are required.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Electrónica

Pantallas

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Absorción de agua	23.0 °C	0.2 % Show Supplier Material materials with Absorción de agua of 0.2 %	ISO 62-1 \| (23°C/saturated)
Densidad	23.0 °C	1.21 g/cm³ Show Supplier Material materials with Densidad of 1.21 g/cm³	ISO 1183
Densidad relativa	23.0 °C	1.21 [-] Show Supplier Material materials with Densidad relativa of 1.21 [-]	ASTM D 792
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	2.7 % Show Supplier Material materials with Elongación of 2.7 %	ISO 527 \| break, 5 mm/min
Hardness, Rockwell R	23.0 °C	121 [-] Show Supplier Material materials with Hardness, Rockwell R of 121 [-]	ASTM D 785
Impact strength, Izod notched, ASTM	23.0 °C	500 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 500 J/m	ASTM D 256 \| notched, 23°C
Módulo de flexión	23.0 °C	4.9 GPa Show Supplier Material materials with Módulo de flexión of 4.9 GPa	ISO 178 \| 2 mm/min
Módulo elástico	23.0 °C	5.6 GPa Show Supplier Material materials with Módulo elástico of 5.6 GPa	ISO 527 \| 1 mm/min
Resistencia a la flexión	23.0 °C	140 MPa Show Supplier Material materials with Resistencia a la flexión of 140 MPa	ISO 178 \| yield, 2 mm/min
Resistencia a la tracción	23.0 °C	112 MPa Show Supplier Material materials with Resistencia a la tracción of 112 MPa	ISO 527 \| break, 5 mm/min
Resistencia al choque, ensayo Charpy entallado	23.0 °C	7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 7 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Resistencia al choque, ensayo Izod entallado	23.0 °C	7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m²	ISO 180/1A \| 80104, 23°C
Resistencia al choque, ensayo Izod no entallado	23.0 °C	27 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 27 kJ/m²	ISO 180/1U \| 80104, 23°C

Aplicaciones térmicas

Property	Temperature	Value	Comment
Coeficiente de dilatación térmica	23.0 °C	3.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3.5E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Coeficiente de dilatación térmica transversal	23.0 °C	6.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.4E-5 1/K	ISO 11359-2 \| 23°C to 80°C
Heat deflection temperature, 1.80 MPa		155 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 155 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Temperatura de flexión bajo carga		155 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 155 °C
Temperatura de reblandecimiento Vicat		161 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 161 °C	ISO 306 \| Rate B/50
Inflamabilidad	Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12

Eléctrico

Property	Temperature	Value	Comment
Índice de seguimiento comparativo	23.0 °C	3 V Show Supplier Material materials with Índice de seguimiento comparativo of 3 V	UL 746A \| (UL) {PLC}

Rheological Properties

Property	Temperature	Value	Comment
Contracción	23.0 °C	0.5 % Show Supplier Material materials with Contracción of 0.5 %	SABIC method \| 3.2 mm
Velocidad de flujo de la masa derretida		20 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 20 g/10min	ASTM D 1238 \| 300°C/5.0 kgf

Technological properties

Property
Application areas	Document Handling
Availability	Europe,Asia,Americas
Processing methods	Drying Temperature: 110 to 120.0°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 8hrs Maximum Moisture Content: 0.02% Melt Temperature: 300 to 325.0°C Nozzle Temperature: 300 to 325.0°C Front - Zone 3 Temperature: 290 to 325.0°C Middle - Zone 2 Temperature: 275 to 320.0°C Rear - Zone 1 Temperature: 265 to 315.0°C Mold Temperature: 80 to 110.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 20 to 100.0rpm Shot to Cylinder Size: 30 to 70.0%
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.