General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.28 % Show Supplier Material materials with Absorción de agua of 0.28 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.34 g/cm³ Show Supplier Material materials with Densidad of 1.34 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.34 [-] Show Supplier Material materials with Densidad relativa of 1.34 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.11 % Show Supplier Material materials with Moisture absorption of 0.11 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 6.8 % Show Supplier Material materials with Elongación of 6.8 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 194 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 194 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 80 J Show Supplier Material materials with Instrumented Impact, Total Energy of 80 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 107 MPa Show Supplier Material materials with Resistencia a la flexión of 107 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 76 MPa Show Supplier Material materials with Resistencia a la tracción of 76 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball pressure temperature | 125 °C Show Supplier Material materials with Ball pressure temperature of 125 °C | IEC 60695-10-2 | approximate maximum | |||
Coeficiente de dilatación térmica | 23.0 °C | 5.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 117 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 117 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 117 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 117 °C | ||||
Temperatura de reblandecimiento Vicat | 137 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 137 °C | ISO 306 | Rate B/50 | |||
Inflamabilidad | Vertical Burn b (12s) passes at: 0.5sec FAR 25.853 <br> OSU peak heat release rate (5 minute test): <55kW/m² FAR 25.853 <br> Vertical Burn a (60s) passes at: 2.4sec FAR 25.853 <br> NBS Smoke Density, Flaming, Dmax: <25- ASTM E 662 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción of 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 5 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 16 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 16 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Aircraft Seating, Aerospace, Air Cabin Interiors, Rail Window Glazing, Sensor, Rail Seating, Personal Computing | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 105°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |