General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 3.5 % Show Supplier Material materials with Absorción de agua of 3.5 % | ASTM D 570 | (23°C/Saturated) |
Densidad relativa | 23.0 °C | 1.08 [-] Show Supplier Material materials with Densidad relativa of 1.08 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 1.19 % Show Supplier Material materials with Moisture absorption of 1.19 % | ASTM D 570 | (50% RH, Equilibrium) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 4 % Show Supplier Material materials with Elongación of 4 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 528 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 528 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 41 J Show Supplier Material materials with Instrumented Impact, Total Energy of 41 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 1.8 GPa Show Supplier Material materials with Módulo de flexión of 1.8 GPa | ISO 178 | 2 mm/min |
Resistencia a la flexión | 23.0 °C | 70 MPa Show Supplier Material materials with Resistencia a la flexión of 70 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 50 MPa Show Supplier Material materials with Resistencia a la tracción of 50 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 20 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Conductividad térmica | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.23 W/(m·K) | ASTM C177 |
Heat deflection temperature, 0.45 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Temperatura de flexión bajo carga | 175 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 175 °C | ||
Temperatura de reblandecimiento Vicat | 240 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 240 °C | ISO 306 | Rate A/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.5 % Show Supplier Material materials with Contracción of 1.5 % | SABIC method |
Contracción transversal | 23.0 °C | 1.3 % Show Supplier Material materials with Contracción transversal of 1.3 % | SABIC method |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Bumper, Interior, Thin wall packaging | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 95 to 105.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |