Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 52 % Show Supplier Material materials with Elongación of 52 % | ASTM D 638 | brk, Type I, 50 mm/min |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 272 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 272 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 3204 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 3204 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 36 J Show Supplier Material materials with Instrumented Impact, at Peak of 36 J | ASTM D 3763 | -30 |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo de flexión of 2.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Resistencia a la flexión | 23.0 °C | 89 MPa Show Supplier Material materials with Resistencia a la flexión of 89 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 56 MPa Show Supplier Material materials with Resistencia a la tracción of 56 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 272 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 272 kJ/m² | ASTM D 256 | notched, 23°C |
Taber Abrasion | 23.0 °C | 19 mg/1000cy Show Supplier Material materials with Taber Abrasion of 19 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ASTM E 831 | -20°C to 150°C |
Heat deflection temperature, 0.45 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 155 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 127 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ASTM D 648 | 6.4 mm, unannealed | |
Temperatura de flexión bajo carga | 127 - 155 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 127 - 155 °C | ||
Temperatura de reblandecimiento Vicat | 232 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 232 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique, Power Boat, Recreational Vehicle, Motorcycle, Laundry Dryer, Weapon, Vertical Body Panel, Wheel Cover, Washing Machine, Exterior Rail Components, Engine Component, Exterior Mirror, Exterior Trim, Heavy Vehicles, Lawn/Garden, Enclosures, Cowl Vent Grille, Door Handle, Building Accessory, Auto Electrical, Auto Aftermarket | |
| Availability | Asia,Americas | |
| Processing methods | Melt Temperature: 275 to 300.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |