| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.58 g/cm³ Show Supplier Material materials with Densidad of 1.58 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.2 % Show Supplier Material materials with Elongación of 1.2 % | ISO 527 | break |
Módulo de flexión | 23.0 °C | 11.9 GPa Show Supplier Material materials with Módulo de flexión of 11.9 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 12.5 GPa Show Supplier Material materials with Módulo elástico of 12.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 238 MPa Show Supplier Material materials with Resistencia a la flexión of 238 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 129 MPa Show Supplier Material materials with Resistencia a la tracción of 129 MPa | ISO 527 | break |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.2E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.2E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 1.80 MPa | 263 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 263 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 220 °C Show Supplier Material materials with Relative temperature index, electrical of 220 °C | UL 746B | |||
Relative temperature index, mechanical impact | 200 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 200 °C | UL 746B | |||
Relative temperature index, mechanical strength | 220 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 220 °C | UL 746B | |||
Temperatura de flexión bajo carga | 263 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 263 °C | ||||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.45mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101283822- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101283821- - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Índice de seguimiento comparativo | 23.0 °C | 4 V Show Supplier Material materials with Índice de seguimiento comparativo of 4 V | UL 746A | (UL) {PLC} |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wiring Devices, Electronic Components | |
| Availability | Europe,Americas | |
| Processing methods | Drying Time: 4hrs | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |