General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.68 g/cm³ Show Supplier Material materials with Densidad of 1.68 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.2 % Show Supplier Material materials with Elongación of 1.2 % | ISO 527 | break |
Módulo de flexión | 23.0 °C | 14 GPa Show Supplier Material materials with Módulo de flexión of 14 GPa | ISO 178 | 2 mm/min |
Resistencia a la flexión | 23.0 °C | 190 MPa Show Supplier Material materials with Resistencia a la flexión of 190 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 182 MPa Show Supplier Material materials with Resistencia a la tracción of 182 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 6 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 21 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 21 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 272 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 272 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 220 °C Show Supplier Material materials with Relative temperature index, electrical of 220 °C | UL 746B | |||
Relative temperature index, mechanical impact | 200 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 200 °C | UL 746B | |||
Relative temperature index, mechanical strength | 220 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 220 °C | UL 746B | |||
Temperatura de flexión bajo carga | 272 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 272 °C | ||||
Inflamabilidad | UL Recognized, 94-5VA Flame Class Rating: ≥3mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.45mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284690- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101283821- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Índice de seguimiento comparativo | 23.0 °C | 4 V Show Supplier Material materials with Índice de seguimiento comparativo of 4 V | UL 746A | (UL) {PLC} |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Pipe/Fitting, Pump, Recreational Vehicle, Wiring Devices, Enclosure/Housing/Cover, Electronic Components, Lawn/Garden, Air Conditioning, Document Handling | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |