General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.107 g/cm³ Show Supplier Material materials with Densidad of 1.107 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 1 % Show Supplier Material materials with Moisture absorption of 1 % | ASTM D 570 | (50% RH, Equilibrium) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 60 % Show Supplier Material materials with Elongación of 60 % | ASTM D 638 | brk, Type I, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo de flexión of 2.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Resistencia a la flexión | 23.0 °C | 95 MPa Show Supplier Material materials with Resistencia a la flexión of 95 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 59 MPa Show Supplier Material materials with Resistencia a la tracción of 59 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 240 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 240 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.26E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.26E-4 1/K | ASTM E 831 | 60°C to 138°C |
Heat deflection temperature, 0.45 MPa | 193 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 193 °C | ASTM D 648 | 6.4 mm, unannealed | |
Temperatura de flexión bajo carga | 193 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 193 °C | ||
Temperatura de reblandecimiento Vicat | 232 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 232 °C | ASTM D 1525 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción of 1.1 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Heavy Vehicles, Head Protection, Energy Absorber, Door Handle, Document Handling, Console, Cladding, Auto Aftermarket, Pump, Small Appliance, Medical Device, Wheel Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Rear - Zone 1 Temperature: 265 to 305.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |