General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.32 - 0.33 [-] Show Supplier Material materials with Coefficient of friction of 0.32 - 0.33 [-] | ||
Coefficient of friction, kinetic | 0.32 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.32 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.33 [-] Show Supplier Material materials with Coefficient of friction, static of 0.33 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.41 g/cm³ Show Supplier Material materials with Densidad of 1.41 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.4 % Show Supplier Material materials with Elongación of 1.4 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 428 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 428 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, at Peak of 8 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 9.7 GPa Show Supplier Material materials with Módulo de flexión of 9.7 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 11.2 GPa Show Supplier Material materials with Módulo elástico of 11.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 172 MPa Show Supplier Material materials with Resistencia a la flexión of 172 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 125 MPa Show Supplier Material materials with Resistencia a la tracción of 125 MPa | ISO 527 | break |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 23 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 23 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Relative temperature index, electrical | 130 °C Show Supplier Material materials with Relative temperature index, electrical of 130 °C | UL 746B | |
Relative temperature index, mechanical impact | 130 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 130 °C | UL 746B | |
Relative temperature index, mechanical strength | 130 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 130 °C | UL 746B | |
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating: 1mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103093471- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 10000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 10000 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Document Handling, Personal Computing | |
Availability | Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |