Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.8 % Show Supplier Material materials with Elongación of 1.8 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 76 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 76 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 8.1 GPa Show Supplier Material materials with Módulo de flexión of 8.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 10.1 GPa Show Supplier Material materials with Módulo elástico of 10.1 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 169 MPa Show Supplier Material materials with Resistencia a la flexión of 169 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 148 MPa Show Supplier Material materials with Resistencia a la tracción of 148 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 76 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 76 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.43E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.43E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.5E-5 1/K | ASTM E 831 | -40°C to 150°C | ||
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Temperatura de flexión bajo carga | 203 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 203 °C | ||||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102158299- - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.3 % Show Supplier Material materials with Contracción of 0.3 % | SABIC method |
Contracción transversal | 23.0 °C | 0.53 % Show Supplier Material materials with Contracción transversal of 0.53 % | SABIC method |
Velocidad de flujo de la masa derretida | 15.4 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 15.4 g/10min | ASTM D 1238 | 337°C/6.6 kgf | |
Velocidad de flujo del volumen derretido | 34 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 34 cm³/10min | ISO 1133 | MVR at 345°C/10.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Semiconductor | |
| Availability | Asia | |
| Processing methods | Melt Temperature: 350 to 400.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |