Propiedades
General
| Property | Temperature | Value |
|---|---|---|
Índice límite de óxigeno | 23.0 °C | 48 % Show Supplier Material materials with Índice límite de óxigeno of 48 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 7 % Show Supplier Material materials with Elongación of 7 % | ISO 527 | break, 5 mm/min |
Módulo de flexión | 23.0 °C | 3.8 GPa Show Supplier Material materials with Módulo de flexión of 3.8 GPa | ISO 178 | 2 mm/min |
Resistencia a la flexión | 23.0 °C | 150 MPa Show Supplier Material materials with Resistencia a la flexión of 150 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 90 MPa Show Supplier Material materials with Resistencia a la tracción of 90 MPa | ISO 527 | break, 5 mm/min |
Taber Abrasion | 23.0 °C | 35 mg/1000cy Show Supplier Material materials with Taber Abrasion of 35 mg/1000cy | SABIC method | CS-17, 1 kg |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4.5E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 4.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Heat deflection temperature, 1.80 MPa | 202 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 202 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Temperatura de flexión bajo carga | 202 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 202 °C | ||||
Temperatura de reblandecimiento Vicat | 222 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 222 °C | ISO 306 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating: 1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221112- - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 17 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, IEC 60093 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components | |
| Availability | Europe,Americas | |
| Processing methods | Melt Temperature: 370 to 410.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |