Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 30 % Show Supplier Material materials with Elongación of 30 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 202 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 202 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, at Peak | 23.0 °C | 40 J Show Supplier Material materials with Instrumented Impact, at Peak of 40 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 0.8 GPa Show Supplier Material materials with Módulo elástico of 0.8 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la flexión | 23.0 °C | 85 MPa Show Supplier Material materials with Resistencia a la flexión of 85 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 55 MPa Show Supplier Material materials with Resistencia a la tracción of 55 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Conductividad térmica | 23.0 °C | 0.25 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.25 W/(m·K) | ASTM C177 | ||
Heat deflection temperature, 0.45 MPa | 185 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 185 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 148 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 148 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Temperatura de flexión bajo carga | 148 - 185 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 148 - 185 °C | ||||
Temperatura de reblandecimiento Vicat | 190 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 190 °C | ISO 306 | Rate B/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating: 1.2mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102330645- - | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Supplier Material materials with Contracción of 1.3 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1 % Show Supplier Material materials with Contracción transversal of 1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 45 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 45 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 5 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min | ISO 1133 | MVR at 280°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Sensor, Wheel Cover, Transmission/Transfer Comp, Traction Motor, Auto Electrical, Electronic Components, Heavy Vehicles | |
| Availability | Asia,Americas | |
| Processing methods | Drying Time: 3 to 4.0hrs | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |