LEXAN™ Copolymer ML0992 - Asia

Want to keep this datasheet? Save it now in your required format

Description

LEXAN ML0992 is a translucent impact modified polycarbonate injection molding (IM) grade with release properties. This resin offers good low temperature ductility in combination with medium flow characteristics, excellent surface aesthetics, excellent knit line strength, and excellent processability with opportunities for shorter IM cycle times compared to standard IM PC resins. LEXAN ML0992 resin is a general purpose product available for wide range of opaque colors and may be an excellent candidate for a broad range of applications. .

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Electrónica

Pantallas

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Densidad	23.0 °C	1.2 g/cm³ Show Supplier Material materials with Densidad of 1.2 g/cm³	ISO 1183
Moisture absorption	23.0 °C	0.1 % Show Supplier Material materials with Moisture absorption of 0.1 %	ISO 62 \| (23°C / 50% RH)

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	5 % Show Supplier Material materials with Elongación of 5 %	ASTM D 638 \| yld, Type I, 50 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	500 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 500 J/m	ASTM D 256 \| notched, -30°C
Módulo de flexión	23.0 °C	2.1 GPa Show Supplier Material materials with Módulo de flexión of 2.1 GPa	ASTM D 790 \| 1.3 mm/min, 50 mm span
Módulo elástico	23.0 °C	2.3 GPa Show Supplier Material materials with Módulo elástico of 2.3 GPa	ASTM D 638 \| 50 mm/min
Resistencia a la flexión	23.0 °C	85 MPa Show Supplier Material materials with Resistencia a la flexión of 85 MPa	ASTM D 790 \| yld, 1.3 mm/min, 50 mm span
Resistencia a la tracción	23.0 °C	57 MPa Show Supplier Material materials with Resistencia a la tracción of 57 MPa	ASTM D 638 \| brk, Type I, 50 mm/min
Resistencia al choque, ensayo Izod entallado	23.0 °C	750 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 750 kJ/m²	ASTM D 256 \| notched, 23°C

Aplicaciones térmicas

Property	Value	Comment
Heat deflection temperature, 1.80 MPa	118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C	ASTM D 648 \| 3.2mm, unannealed
Relative temperature index, electrical	80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C	UL 746B
Relative temperature index, mechanical impact	80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C	UL 746B
Relative temperature index, mechanical strength	80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C	UL 746B
Temperatura de flexión bajo carga	118 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 118 °C
Inflamabilidad	UL Recognized, 94HB Flame Class Rating: 0.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103670399- -

Rheological Properties

Property	Temperature	Value	Comment
Contracción	23.0 °C	0.4 % Show Supplier Material materials with Contracción of 0.4 %	SABIC method \| 3.2 mm
Contracción transversal	23.0 °C	0.4 % Show Supplier Material materials with Contracción transversal of 0.4 %	SABIC method \| 3.2 mm
Velocidad de flujo de la masa derretida		14 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 14 g/10min	ASTM D 1238 \| 300°C/1.2 kgf
Velocidad de flujo del volumen derretido		13 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min	ISO 1133 \| MVR at 300°C/1.2 kg

Technological properties

Property
Application areas	Wireless Communications, Personal Computing
Availability	Asia
Processing methods	Drying Temperature: 120°C Drying Time: 3 to 4.0hrs Drying Time (Cumulative): 48hrs Maximum Moisture Content: 0.02% Melt Temperature: 295 to 315.0°C Nozzle Temperature: 290 to 310.0°C Front - Zone 3 Temperature: 295 to 315.0°C Middle - Zone 2 Temperature: 280 to 305.0°C Rear - Zone 1 Temperature: 270 to 295.0°C Mold Temperature: 70 to 95.0°C Back Pressure: 0.3 to 0.7MPa Screw Speed: 40 to 70.0rpm Shot to Cylinder Size: 40 to 60.0% Vent Depth: 0.025 to 0.076mm
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.