Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.29 g/cm³ Show Supplier Material materials with Densidad of 1.29 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.29 [-] Show Supplier Material materials with Densidad relativa of 1.29 [-] | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 92 % Show Supplier Material materials with Elongación of 92 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 123 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 123 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 74 J Show Supplier Material materials with Instrumented Impact, Total Energy of 74 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo elástico of 2.3 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 96 MPa Show Supplier Material materials with Resistencia a la flexión of 96 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 65 MPa Show Supplier Material materials with Resistencia a la tracción of 65 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 27 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 27 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 13 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball pressure temperature | 125 °C Show Supplier Material materials with Ball pressure temperature of 125 °C | IEC 60695-10-2 | approximate maximum | |||
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.3E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 131 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 131 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 131 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 131 °C | ||||
Temperatura de reblandecimiento Vicat | 154 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 154 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | OSU peak heat release rate (5 minute test): <65kW/m² FAR 25.853 <br> NBS Smoke Density, Flaming, Dmax: <40- ASTM E 662 <br> Vertical Burn a (60s) passes at: <15sec FAR 25.853 <br> Vertical Burn b (12s) passes at: <15sec FAR 25.853 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción of 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 10 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 10 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 44 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 44 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Aircraft Seating | |
| Availability | Americas | |
| Processing methods | Screw Speed: 40 to 70.0rpm | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |