General
Property | Value | Comment |
---|---|---|
Coefficient of friction | 0.67 - 0.87 [-] Show Supplier Material materials with Coefficient of friction of 0.67 - 0.87 [-] | |
Coefficient of friction, kinetic | 0.67 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.67 [-] | ASTM D 3702 Modified: Manual |
Coefficient of friction, static | 0.87 [-] Show Supplier Material materials with Coefficient of friction, static of 0.87 [-] | ASTM D 3702 Modified: Manual |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.9 % Show Supplier Material materials with Elongación of 2.9 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 95 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 95 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1000 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1000 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 8.6 GPa Show Supplier Material materials with Módulo de flexión of 8.6 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 10.2 GPa Show Supplier Material materials with Módulo elástico of 10.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 235 MPa Show Supplier Material materials with Resistencia a la flexión of 235 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 155 MPa Show Supplier Material materials with Resistencia a la tracción of 155 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 75 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.4E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9.6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 200 - 215 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 200 - 215 °C | ||
Temperatura de reblandecimiento Vicat | 210 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 210 °C | ISO 306 | Rate B/50 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wiring Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |