Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.3 % Show Supplier Material materials with Absorción de agua of 0.3 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Densidad of 1.44 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.43 [-] Show Supplier Material materials with Densidad relativa of 1.43 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.12 % Show Supplier Material materials with Moisture absorption of 0.12 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Supplier Material materials with Elongación of 2.5 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 133 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 133 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 852 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 852 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 17 J Show Supplier Material materials with Instrumented Impact, Total Energy of 17 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 7.8 GPa Show Supplier Material materials with Módulo de flexión of 7.8 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 7.9 GPa Show Supplier Material materials with Módulo elástico of 7.9 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 182 MPa Show Supplier Material materials with Resistencia a la flexión of 182 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 115 MPa Show Supplier Material materials with Resistencia a la tracción of 115 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 11 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 49 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 49 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | 80*10*3, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 37 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 37 kJ/m² | ISO 180/1U | unnotched 80*10*3, 23°C, |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Coeficiente de dilatación térmica | 23.0 °C | 3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Heat deflection temperature, 0.45 MPa | 130 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 130 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 129 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 129 - 130 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 129 - 130 °C | ||
Temperatura de reblandecimiento Vicat | 143 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 143 °C | ISO 306 | Rate B/120 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción transversal of 0.1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 16 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 16 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 18 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 18 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wireless Communications, Personal Computing, Photo/Video Camera, Building Accessory | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Vent Depth: 0.025 to 0.076mm | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |