FLEX NORYL™ Resin WCD801A - Asia

Want to keep this datasheet? Save it now in your required format

Description

FLEX NORYL™ WCD801A resin is a flexible, non-reinforced, migration improved, extrudable blend of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE). This material contains non-halogenated flame retardant and performance capable of meeting UL VW-1 requirements, 80C end use temperature rating, and heat deformation performance as defined by UL 1581. FLEX NORYL WCD801A resin is intended for evaluation in wire insulation and cable jacket applications in dark colors. It has a Shore A Hardness reading of 80 and exhibits superior thermal stability, very low water absorption, good electric properties, and low specific gravity. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Ingeniería eléctrica

Electrónica

Pantallas

Automotriz

Bienes de consumo

Electrodomésticos para el hogar

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Densidad relativa	23.0 °C	1.1 [-] Show Supplier Material materials with Densidad relativa of 1.1 [-]	ASTM D 792 \|
Índice límite de óxigeno	23.0 °C	26 % Show Supplier Material materials with Índice límite de óxigeno of 26 %

Mecánica

Property	Temperature	Value	Comment
Dureza Shore A	23.0 °C	80 [-] Show Supplier Material materials with Dureza Shore A of 80 [-]	ASTM D 2240 \| 30S reading
Elongación	23.0 °C	119 % Show Supplier Material materials with Elongación of 119 %	ISO 527 \| break, 50 mm/min
Módulo de flexión	23.0 °C	0.1 GPa Show Supplier Material materials with Módulo de flexión of 0.1 GPa	ISO 178 \| 12.5 mm/min
Resistencia a la tracción	23.0 °C	13 MPa Show Supplier Material materials with Resistencia a la tracción of 13 MPa	ISO 527 \| break, 50 mm/min

Aplicaciones térmicas

Property	Value	Comment
Brittleness temperature	-40 °C Show Supplier Material materials with Brittleness temperature of -40 °C	<, ASTM D 746
Inflamabilidad	Smoke Density on 0.5mm plaque, Non-flame, Ds, max: 95- ASTM E 662 <br> Smoke Density on 0.5mm plaque, Flame, Ds, max: 142- ASTM E 662

Eléctrico

Property	Temperature	Value	Comment
Constante dieléctrica, 1 MHz	23.0 °C	2.8 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 2.8 [-]	IEC 60250
Dielectric constant, 60Hz	23.0 °C	2.8 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 2.8 [-]	IEC 60250 \| 50/60 Hz
Dissipation factor, 1MHz	23.0 °C	4E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 4E-3 [-]	IEC 60250
Dissipation factor, 50Hz	23.0 °C	0.03 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.03 [-]	IEC 60250 \| 50/60 Hz
Rigidez dieléctrica	23.0 °C	23 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 23 kV/mm	IEC 60243-1 \| in oil, 2.0mm
Volume resistivity	23.0 °C	3.80E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 3.80E+15 Ω·cm	IEC 60093
Índice de seguimiento comparativo	23.0 °C	600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V	IEC 60112 \|

Rheological Properties

Property	Value	Comment
Velocidad de flujo de la masa derretida	11 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 11 g/10min	ASTM D 1238 \| 250°C/5.0 kgf

Technological properties

Property
Application areas	Wireless Communications, Personal Computing, Enclosure/Housing/Cover, Heavy Vehicles, Freezer, Wire & cable
Availability	Americas
Processing methods	Drying Time: 5 to 7.0hrs Drying Time (Cumulative): 12hrs Screen Pack: 150 to 100.0- Water Bath Temperature: 15 to 60.0°C Drying Temperature: 75 to 85.0°C Head Zone Temperature: 220 to 250.0°C Conductor Pre-heat Temperature: 25 to 120.0°C Middle Zone Temperatures: 220 to 250.0°C Die Temperature: 220 to 250.0°C Cooling Water Air Gap: 100 to 200.0mm Maximum Moisture Content: 0.02% Feed Zone Temperature: 180 to 220.0°C Cross-head Temperature: 220 to 250.0°C Screw Speed: 15 to 85.0rpm Melt Temperature: 220 to 250.0°C Neck Temperature: 220 to 250.0°C Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.