General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Supplier Material materials with Absorción de agua of 0.2 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.11 g/cm³ Show Supplier Material materials with Densidad of 1.11 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.11 [-] Show Supplier Material materials with Densidad relativa of 1.11 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.05 % Show Supplier Material materials with Moisture absorption of 0.05 % | ISO 62 | (23°C / 50% RH) |
Índice límite de óxigeno | 23.0 °C | 33 % Show Supplier Material materials with Índice límite de óxigeno of 33 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 8.3 % Show Supplier Material materials with Elongación of 8.3 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 300 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 300 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 100 MPa Show Supplier Material materials with Resistencia a la flexión of 100 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 58 MPa Show Supplier Material materials with Resistencia a la tracción of 58 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 14 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 124 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 124 °C | ||||
Temperatura de reblandecimiento Vicat | 143 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 143 °C | ISO 306 | Rate B/50 | |||
Inflamabilidad | Ds_4min: 70- ISO 5659-2 <br> Lateral Flame Spread, CFE: 20kW/m² ISO 5658-2 <br> M1 Flame Class Rating: 2mm NF P 92501 <br> Glow Wire Ignitability Temperature, 1.0 mm: 775°C IEC 60695-2-13 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Toxicity (3 mm): 21.76- NF X70-100 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (3.2 mm): 30- ASTM E 662 <br> Heat Release, MAHRE: 33.6kW/m² ISO 5660-1 <br> Toxicity: 0- ISO 5659-2 <br> F1 Class Smoke and Toxicity Rating: 3mm NF F16-101 <br> NBS Smoke Density, Flaming, 20 min (3.2 mm): 120- ASTM E 662 <br> Glow Wire Flammability Index, 1.0 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 <br> Glow Wire Ignitability Temperature, 1.5 mm: 775°C IEC 60695-2-13 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100050086- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 2.7 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 2.9E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2.9E-3 [-] | IEC 60250 |
Rigidez dieléctrica | 23.0 °C | 34.1 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 34.1 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Sheet resistivity, ROA | 23.0 °C | 1.25E+18 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.25E+18 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 7.62E+17 Ω·cm Show Supplier Material materials with Volume resistivity of 7.62E+17 Ω·cm | IEC 60093 | |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 5.6 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5.6 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 5 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Exterior Rail Components, Fuel Cell, Rail, Wiring Devices, Wire & cable | |
Availability | Europe,Asia,Americas | |
Processing methods | Barrel - Zone 1 Temperature: 220 to 260.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |