General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.58 % Show Supplier Material materials with Absorción de agua of 0.58 % | ISO 62-1 | (23°C/24hrs) |
Densidad | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Densidad of 1.19 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.19 [-] Show Supplier Material materials with Densidad relativa of 1.19 [-] | ASTM D 792 |
Índice límite de óxigeno | 23.0 °C | 48 % Show Supplier Material materials with Índice límite de óxigeno of 48 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Shore D | 23.0 °C | 72 [-] Show Supplier Material materials with Dureza Shore D of 72 [-] | ASTM D 2240 |
Elongación | 23.0 °C | 74 % Show Supplier Material materials with Elongación of 74 % | ISO 527 | break, 50 mm/min |
Módulo de flexión | 23.0 °C | 1.3 GPa Show Supplier Material materials with Módulo de flexión of 1.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 1.4 GPa Show Supplier Material materials with Módulo elástico of 1.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 55 MPa Show Supplier Material materials with Resistencia a la flexión of 55 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 41 MPa Show Supplier Material materials with Resistencia a la tracción of 41 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 25 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 25 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Taber Abrasion | 23.0 °C | 50 mg/1000cy Show Supplier Material materials with Taber Abrasion of 50 mg/1000cy | ASTM D 1044 | CS-17, 1 kg |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 144 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 144 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 144 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 144 °C | ||
Temperatura de reblandecimiento Vicat | 167 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 167 °C | ISO 306 | Rate B/120 | |
Temperatura de transición del vidrio | 195 °C Show Supplier Material materials with Temperatura de transición del vidrio of 195 °C | DMA | matrix | |
Inflamabilidad | UL Compliant, 94V-0 Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.02 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.02 [-] | ASTM D 150 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.14 [-] Show Supplier Material materials with Constante dieléctrica, 100 Hz of 3.14 [-] | ASTM D 150 |
Dielectric constant, 1KHz | 23.0 °C | 3 [-] Show Supplier Material materials with Dielectric constant, 1KHz of 3 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 0.01 [-] | ASTM D 150 |
Dissipation factor, 100kHz | 23.0 °C | 6.4E-3 [-] Show Supplier Material materials with Dissipation factor, 100kHz of 6.4E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 5.5E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 5.5E-3 [-] | ASTM D 150 | |
Rigidez dieléctrica | 23.0 °C | 16.6 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 16.6 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.86 % Show Supplier Material materials with Contracción of 0.86 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 8.6 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 8.6 g/10min | ASTM D 1238 | 295°C/6.6 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Fluid Delivery, Enclosure/Housing/Cover, Aerospace, Wire & cable | |
Availability | Europe,Americas | |
Processing methods | Drying Time (Cumulative): 8hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |