NORYL™ Resin NH4030B - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ NH4030B resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high flow, injection moldable and extrusion grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm along with lower smoke production upon burning and low specific gravity for light-weight parts. NORYL NH4030B resin may be an excellent candidate for rail interior, electrical conduit, cable management, and ceiling-mounted electric applications.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Electrónica

Pantallas

Ferrocarriles

Construcción

Aeroespacial

Bienes de consumo

General Appliances

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Absorción de agua	23.0 °C	0.27 % Show Supplier Material materials with Absorción de agua of 0.27 %	ISO 62-1 \| (23°C/saturated)
Densidad	23.0 °C	1.11 g/cm³ Show Supplier Material materials with Densidad of 1.11 g/cm³	ISO 1183
Densidad relativa	23.0 °C	1.11 [-] Show Supplier Material materials with Densidad relativa of 1.11 [-]	ASTM D 792 \|
Moisture absorption	23.0 °C	0.04 % Show Supplier Material materials with Moisture absorption of 0.04 %	ISO 62 \| (23°C / 50% RH)

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	4 % Show Supplier Material materials with Elongación of 4 %	ISO 527 \| yield, 50 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	200 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 200 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	46 J Show Supplier Material materials with Instrumented Impact, Total Energy of 46 J	ASTM D 3763 \| 23°C
Módulo de flexión	23.0 °C	2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa	ISO 178 \| 2 mm/min
Módulo elástico	23.0 °C	2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa	ISO 527 \| 1 mm/min
Resistencia a la flexión	23.0 °C	90 MPa Show Supplier Material materials with Resistencia a la flexión of 90 MPa	ISO 178 \| yield, 2 mm/min
Resistencia a la tracción	23.0 °C	54 MPa Show Supplier Material materials with Resistencia a la tracción of 54 MPa	ISO 527 \| yield, 50 mm/min
Resistencia al choque, ensayo Charpy entallado	23.0 °C	19 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 19 kJ/m²	ISO 179/1eA \| V-notch Edgew 80104 sp=62mm, 23°C
Resistencia al choque, ensayo Izod entallado	23.0 °C	15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 15 kJ/m²	ISO 180/1A \| 80104, 23°C

Aplicaciones térmicas

Property	Temperature	Value	Comment
Coeficiente de dilatación térmica	23.0 °C	8.39E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.39E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coeficiente de dilatación térmica transversal	23.0 °C	8.54E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8.54E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature, 1.80 MPa		107 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 107 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Temperatura de flexión bajo carga		107 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 107 °C
Temperatura de reblandecimiento Vicat		127 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 127 °C	ISO 306 \| Rate B/50
Inflamabilidad	Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Vertical Burn a (60s, 1.52mm) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 29- ASTM E 662 <br> Vertical Burn b (12s, 1.52mm) passes at: 4sec FAR 25.853 <br> NBS Smoke Density, Flaming, 20 min (3.2 mm): 126- ASTM E 662 <br> NBS Smoke Density, Flaming, 4 min (3.2 mm): 35- ASTM E 662 <br> Draeger Tube Toxicity, Non-Flaming (1.52mm): Pass- AITM 3.0005, ABD0031 <br> Draeger Tube Toxicity, Flaming (1.52mm): Pass- AITM 3.0005, ABD0031 <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=100880699- -

Rheological Properties

Property	Temperature	Value	Comment
Contracción	23.0 °C	0.5 % Show Supplier Material materials with Contracción of 0.5 %	SABIC method \| 3.2 mm
Velocidad de flujo de la masa derretida		42.7 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 42.7 g/10min	ASTM D 1238 \| 300°C/5.0 kgf
Velocidad de flujo del volumen derretido		41 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 41 cm³/10min	ISO 1133 \| MVR at 300°C/5.0 kg

Technological properties

Property
Application areas	Displays, Air Conditioning, Air Cabin Interiors, Vending Machine, Rail Cabin Interiors, Rail Seating, Rail, Interior Rail Components
Availability	Europe,Asia,Americas
Processing methods	Barrel - Zone 1 Temperature: 215 to 250.0°C Die Temperature: 215 to 250.0°C Front - Zone 3 Temperature: 250 to 290.0°C Roll Stack Temp - Top: 90 to 150.0°C Roll Stack Temp - Bottom: 90 to 150.0°C Drying Time (Cumulative): 12hrs Calibrator Temperature: 30 to 60.0°C Shot to Cylinder Size: 30 to 70.0% Drying Time (Cumulative): 12hrs Barrel - Zone 4 Temperature: 215 to 250.0°C Adapter Temperature: 215 to 250.0°C Maximum Moisture Content: 0.07% Drying Time: 2 to 4.0hrs Barrel - Zone 1 Temperature: 215 to 250.0°C Hopper Temperature: 80 to 120.0°C Water Bath Temperature: 30 to 50.0°C Barrel - Zone 3 Temperature: 215 to 250.0°C Barrel - Zone 2 Temperature: 215 to 250.0°C Roll Stack Temp - Middle: 90 to 150.0°C Drying Temperature: 95 to 105.0°C Middle - Zone 2 Temperature: 240 to 280.0°C Melt Temperature: 215 to 250.0°C Die Temperature: 215 to 250.0°C Mold Temperature: 65 to 100.0°C Vent Depth: 0.038 to 0.051mm Adapter Temperature: 215 to 250.0°C Nozzle Temperature: 260 to 290.0°C Back Pressure: 0.3 to 0.7MPa Barrel - Zone 2 Temperature: 215 to 250.0°C Drying Temperature: 95 to 105.0°C Screw Speed: 20 to 100.0rpm Rear - Zone 1 Temperature: 225 to 275.0°C Maximum Moisture Content: 0.07% Drying Time: 2 to 4.0hrs Drying Time: 2 to 4.0hrs Melt Temperature: 215 to 250.0°C Maximum Moisture Content: 0.07% Barrel - Zone 4 Temperature: 215 to 250.0°C Barrel - Zone 3 Temperature: 215 to 250.0°C Drying Time (Cumulative): 12hrs Melt Temperature: 260 to 290.0°C Drying Temperature: 95 to 105.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.