NORYL™ Resin LS6010 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ LS6010 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high performance, injection moldable and extrudable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.5mm. NORYL LS6010 resin features low smoke production upon burning, high heat resistance, very low specific gravity, enhanced resistance to melting and dripping and meets the requirements of FAR 25.853. In addition, this material is heat stabilized and impact modified. It is an excellent candidate for aerospace interior applications such as rub strips, seat track covers, cable guides, switch panels, conduit, wall/ceiling mounted electronics, and parts machined from slab stock.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Ferrocarriles

Aeroespacial

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Absorción de agua	23.0 °C	0.2 % Show Supplier Material materials with Absorción de agua of 0.2 %	ISO 62-1 \| (23°C/saturated)
Densidad	23.0 °C	1.11 g/cm³ Show Supplier Material materials with Densidad of 1.11 g/cm³	ISO 1183
Densidad relativa	23.0 °C	1.11 [-] Show Supplier Material materials with Densidad relativa of 1.11 [-]	ASTM D 792 \|
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	8.3 % Show Supplier Material materials with Elongación of 8.3 %	ISO 527 \| break, 50 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m	ASTM D 256 \| notched, -30°C
Instrumented Impact, Total Energy	23.0 °C	52 J Show Supplier Material materials with Instrumented Impact, Total Energy of 52 J	ASTM D 3763 \| 23°C
Módulo de flexión	23.0 °C	2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa	ISO 178 \| 2 mm/min
Módulo elástico	23.0 °C	2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa	ISO 527 \| 1 mm/min
Resistencia a la flexión	23.0 °C	100 MPa Show Supplier Material materials with Resistencia a la flexión of 100 MPa	ISO 178 \| yield, 2 mm/min
Resistencia a la tracción	23.0 °C	58 MPa Show Supplier Material materials with Resistencia a la tracción of 58 MPa	ISO 527 \| break, 50 mm/min
Resistencia al choque, ensayo Charpy entallado	23.0 °C	20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 20 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Resistencia al choque, ensayo Izod entallado	23.0 °C	18 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 18 kJ/m²	ISO 180/1A \| notched 80104, 23°C

Aplicaciones térmicas

Property	Temperature	Value	Comment
Coeficiente de dilatación térmica	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coeficiente de dilatación térmica transversal	23.0 °C	6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature, 1.80 MPa		124 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 124 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Temperatura de flexión bajo carga		124 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 124 °C
Temperatura de reblandecimiento Vicat		146 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 146 °C	ISO 306 \| Rate B/120
Inflamabilidad	Vertical Burn b (12s, 1.52mm) passes at: 4sec FAR 25.853 <br> Flame Spread Index (1.52mm): 15- ASTM E 162 <br> NBS Smoke Density, Flaming, 4 min (1.52mm): 30- ASTM E 662 <br> Vertical Burn a (60s, 1.52mm) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Non-Flaming, 4 min (1.52mm): 7- ASTM E 662 <br> Draeger Tube Toxicity, Non-Flaming (1.52mm): Pass- Based on ASTM E 662 <br> Draeger Tube Toxicity, Flaming (1.52mm): Pass- Based on ASTM E 662

Rheological Properties

Property	Temperature	Value	Comment
Contracción	23.0 °C	0.5 % Show Supplier Material materials with Contracción of 0.5 %	SABIC method \| 3.2 mm
Velocidad de flujo de la masa derretida		5.6 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5.6 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Velocidad de flujo del volumen derretido		5 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 5 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg

Technological properties

Property
Application areas	Air Cabin Interiors, Aerospace, Aircraft Seating, Interior Rail Components
Availability	Europe,Asia,Americas
Processing methods	Drying Time (Cumulative): 12hrs Drying Temperature: 95 to 105.0°C Calibrator Temperature: 30 to 60.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Barrel - Zone 2 Temperature: 220 to 260.0°C Mold Temperature: 65 to 100.0°C Adapter Temperature: 220 to 260.0°C Barrel - Zone 3 Temperature: 220 to 260.0°C Barrel - Zone 4 Temperature: 220 to 260.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Roll Stack Temp - Bottom: 90 to 150.0°C Nozzle Temperature: 295 to 305.0°C Front - Zone 3 Temperature: 295 to 305.0°C Water Bath Temperature: 30 to 50.0°C Adapter Temperature: 220 to 260.0°C Maximum Moisture Content: 0.07% Die Temperature: 220 to 260.0°C Roll Stack Temp - Middle: 90 to 150.0°C Hopper Temperature: 80 to 120.0°C Drying Temperature: 95 to 105.0°C Roll Stack Temp - Top: 90 to 150.0°C Maximum Moisture Content: 0.07% Drying Time: 2 to 4.0hrs Drying Time (Cumulative): 12hrs Drying Time: 2 to 4.0hrs Barrel - Zone 3 Temperature: 220 to 260.0°C Melt Temperature: 220 to 260.0°C Screw Speed: 40 to 80.0rpm Barrel - Zone 2 Temperature: 220 to 260.0°C Drying Temperature: 95 to 105.0°C Shot to Cylinder Size: 30 to 70.0% Melt Temperature: 220 to 260.0°C Drying Time: 2 to 4.0hrs Rear - Zone 1 Temperature: 280 to 295.0°C Melt Temperature: 280 to 305.0°C Barrel - Zone 1 Temperature: 220 to 260.0°C Die Temperature: 220 to 260.0°C Middle - Zone 2 Temperature: 290 to 300.0°C Drying Time (Cumulative): 12hrs
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.