General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad relativa | 23.0 °C | 0.99 [-] Show Supplier Material materials with Densidad relativa of 0.99 [-] | ASTM D 792 | |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 75 % Show Supplier Material materials with Elongación of 75 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 534 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 534 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 37 J Show Supplier Material materials with Instrumented Impact, Total Energy of 37 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 1.4 GPa Show Supplier Material materials with Módulo de flexión of 1.4 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 1.4 GPa Show Supplier Material materials with Módulo elástico of 1.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 51 MPa Show Supplier Material materials with Resistencia a la flexión of 51 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 35 MPa Show Supplier Material materials with Resistencia a la tracción of 35 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 534 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 534 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.62E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.62E-4 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.72E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9.72E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 112 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 112 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 85 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ASTM D 648 | 3.2mm, unannealed | |||
Temperatura de flexión bajo carga | 85 - 112 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 85 - 112 °C | ||||
Temperatura de reblandecimiento Vicat | 131 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 131 °C | ISO 306 | Rate A/50 | |||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221243- - |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción of 0.6 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción transversal of 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 14 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 14 g/10min | ASTM D 1238 | 260°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 12 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 12 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Water Treatment/Filtration | |
Availability | Americas | |
Processing methods | Screw Speed: 20 to 100.0rpm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |