General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 3.5 % Show Supplier Material materials with Absorción de agua of 3.5 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.08 g/cm³ Show Supplier Material materials with Densidad of 1.08 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.19 % Show Supplier Material materials with Moisture absorption of 1.19 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 4 % Show Supplier Material materials with Elongación of 4 % | ISO 527 | yield, 50 mm/min |
Hardness, Ball Indentation | 23.0 °C | 80 MPa Show Supplier Material materials with Hardness, Ball Indentation of 80 MPa | ISO 2039-1 | H358/30 |
Módulo de flexión | 23.0 °C | 1.8 GPa Show Supplier Material materials with Módulo de flexión of 1.8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2 GPa Show Supplier Material materials with Módulo elástico of 2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 70 MPa Show Supplier Material materials with Resistencia a la flexión of 70 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 45 MPa Show Supplier Material materials with Resistencia a la tracción of 45 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 45 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 20 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 20 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Conductividad térmica | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.23 W/(m·K) | ISO 8302 |
Heat deflection temperature, 0.45 MPa | 175 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 175 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |
Temperatura de flexión bajo carga | 175 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 175 °C | ||
Temperatura de reblandecimiento Vicat | 180 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 180 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.4 % Show Supplier Material materials with Contracción of 1.4 % | SABIC method | on tensile bar |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Auto Aftermarket | |
Availability | Europe | |
Processing methods | Melt Temperature: 290 to 320.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |