Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 3.5 % Show Supplier Material materials with Absorción de agua of 3.5 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.09 g/cm³ Show Supplier Material materials with Densidad of 1.09 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.1 [-] Show Supplier Material materials with Densidad relativa of 1.1 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 1.2 % Show Supplier Material materials with Moisture absorption of 1.2 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 7.5 % Show Supplier Material materials with Elongación of 7.5 % | ISO 527 | yield, 50 mm/min |
Hardness, Ball Indentation | 23.0 °C | 90 MPa Show Supplier Material materials with Hardness, Ball Indentation of 90 MPa | ISO 2039-1 | H358/30 |
Impact strength, Izod notched, ASTM | 23.0 °C | 280 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 280 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2 GPa Show Supplier Material materials with Módulo de flexión of 2 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.1 GPa Show Supplier Material materials with Módulo elástico of 2.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 80 MPa Show Supplier Material materials with Resistencia a la flexión of 80 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 55 MPa Show Supplier Material materials with Resistencia a la tracción of 55 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 30 kJ/m² | ISO 179/2C | 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 15 kJ/m² | ISO 180/1A | 80*10*4, -30°C |
Taber Abrasion | 23.0 °C | 15 mg/1000cy Show Supplier Material materials with Taber Abrasion of 15 mg/1000cy | SABIC method | CS-17, 1 kg |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coeficiente de dilatación térmica | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Conductividad térmica | 23.0 °C | 0.23 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.23 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 0.45 MPa | 180 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 180 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Temperatura de flexión bajo carga | 180 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 180 °C | ||||
Temperatura de reblandecimiento Vicat | 245 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 245 °C | ISO 306 | Rate A/50 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 2.7 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 2.7 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.5 [-] | IEC 60250 | 50/60 Hz |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.07 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.07 [-] | IEC 60250 | 50/60 Hz |
Rigidez dieléctrica | 23.0 °C | 20 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 20 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Índice de seguimiento comparativo | 23.0 °C | 600 V Show Supplier Material materials with Índice de seguimiento comparativo of 600 V | IEC 60112 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Supplier Material materials with Contracción of 1.3 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción transversal of 1.1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 12 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 12 g/10min | ASTM D 1238 | 280°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 11 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 11 cm³/10min | ISO 1133 | MVR at 280°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Applique, Wheel Cover, Auto Aftermarket, Console, Data Management, Exterior Trim, Heavy Vehicles, Enclosures, Electronic Components | |
| Availability | Europe | |
| Processing methods | Mold Temperature: 80 to 120.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |