Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 50 % Show Supplier Material materials with Elongación of 50 % | ASTM D 638 | brk, Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 106 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 106 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, at Peak | 23.0 °C | 40 J Show Supplier Material materials with Instrumented Impact, at Peak of 40 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Resistencia a la flexión | 23.0 °C | 99 MPa Show Supplier Material materials with Resistencia a la flexión of 99 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 66 MPa Show Supplier Material materials with Resistencia a la tracción of 66 MPa | ASTM D 638 | yld, Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 176 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 176 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 9.54E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 9.54E-5 1/K | ASTM E 831 | -20°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8.1E-5 1/K | ASTM E 831 | -20°C to 150°C |
Heat deflection temperature, 0.45 MPa | 204 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 204 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 6.4 mm, unannealed | |
Temperatura de flexión bajo carga | 125 - 204 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 125 - 204 °C | ||
Temperatura de reblandecimiento Vicat | 245 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 245 °C | ASTM D 1525 | Rate B/50 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 2.76 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 2.76 [-] | ASTM D 150 |
Dielectric constant, 60Hz | 23.0 °C | 3.27 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.27 [-] | ASTM D 150 | 50/60 Hz |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 | |
Dissipation factor, 50Hz | 23.0 °C | 0.04 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.04 [-] | ASTM D 150 | 50/60 Hz |
Rigidez dieléctrica | 23.0 °C | 25.5 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 25.5 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Sheet resistivity, ROA | 23.0 °C | 1.70E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.70E+16 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 4.40E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 4.40E+16 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Supplier Material materials with Contracción of 1.3 % | SABIC method | 3.2 mm |
Technological properties
Property | ||
---|---|---|
Application areas | Wheel Cover, Plumbing, Door Handle, Enclosures | |
Availability | Asia | |
Processing methods | Rear - Zone 1 Temperature: 255 to 295.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |