General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.25 % Show Supplier Material materials with Absorción de agua of 0.25 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.2 g/cm³ Show Supplier Material materials with Densidad of 1.2 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.2 [-] Show Supplier Material materials with Densidad relativa of 1.2 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.25 % Show Supplier Material materials with Moisture absorption of 0.25 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 7 % Show Supplier Material materials with Elongación of 7 % | ISO 527 | yield, 50 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 145 MPa Show Supplier Material materials with Hardness, Ball Indentation of 145 MPa | ISO 2039-1 | H358/30 | ||
Hardness, Rockwell R | 23.0 °C | 125 [-] Show Supplier Material materials with Hardness, Rockwell R of 125 [-] | ISO 2039-2 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 75 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 75 J/m | ASTM D 256 | notched, -30°C | ||
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 105 MPa Show Supplier Material materials with Resistencia a la flexión of 105 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 60 MPa Show Supplier Material materials with Resistencia a la tracción of 60 MPa | ISO 527 | break, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Izod no entallado | ISO 180/1U | unnotched 80*10*3, 23°C, |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Conductividad térmica | 23.0 °C | 0.2 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.2 W/(m·K) | ASTM C177 | @ 25 °C |
Heat deflection temperature, 0.45 MPa | 150 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 150 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 138 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 138 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 138 - 150 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 138 - 150 °C | ||
Temperatura de reblandecimiento Vicat | 155 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 155 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción of 0.6 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 37 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 37 g/10min | ASTM D 1238 | 300°C/2.16 kgf | |
Velocidad de flujo del volumen derretido | 85 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 85 cm³/10min | ISO 1133 | MVR at 330°C/2.16kg |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover | |
Availability | Europe,Asia,Americas | |
Processing methods | Rear - Zone 1 Temperature: 270 to 315.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |