Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.33 g/cm³ Show Supplier Material materials with Densidad of 1.33 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.33 [-] Show Supplier Material materials with Densidad relativa of 1.33 [-] | ASTM D 792 | |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Elongación | 23.0 °C | 95 % Show Supplier Material materials with Elongación of 95 % | ISO 527 | break, 50 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 130 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 130 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C | ||
Módulo de flexión | 23.0 °C | 2.5 GPa Show Supplier Material materials with Módulo de flexión of 2.5 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo elástico of 2.6 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 105 MPa Show Supplier Material materials with Resistencia a la flexión of 105 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 70 MPa Show Supplier Material materials with Resistencia a la tracción of 70 MPa | ISO 527 | break, 50 mm/min | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | 80*10*3, 23°C | ||
Resistencia al choque, ensayo Charpy entallado | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Izod no entallado | ISO 180/1U | unnotched 80*10*3, 23°C, | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 104 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 104 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 94 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 94 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 94 - 104 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 94 - 104 °C | ||||
Temperatura de reblandecimiento Vicat | 113 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 113 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | NBS Smoke Density, Flaming, Dmax: <75- ASTM E 662 <br> OSU peak heat release rate (5 minute test): <55kW/m² FAR 25.853 <br> Vertical Burn a (60s) passes at: 1sec FAR 25.853 | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method |
Contracción transversal | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción transversal of 0.5 % | SABIC method |
Velocidad de flujo de la masa derretida | 9 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 9 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 10 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 10 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Air Cabin Interiors, Aircraft Seating | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Mold Temperature: 50 to 80.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |