General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.39 % Show Supplier Material materials with Absorción de agua of 0.39 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.34 g/cm³ Show Supplier Material materials with Densidad of 1.34 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.34 [-] Show Supplier Material materials with Densidad relativa of 1.34 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.17 % Show Supplier Material materials with Moisture absorption of 0.17 % | ISO 62 | (23°C / 50% RH) |
Índice límite de óxigeno | 23.0 °C | 49 % Show Supplier Material materials with Índice límite de óxigeno of 49 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 50 % Show Supplier Material materials with Elongación of 50 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 115 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 115 J/m | ASTM D 256 |
Módulo de flexión | 23.0 °C | 2.8 GPa Show Supplier Material materials with Módulo de flexión of 2.8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo elástico of 3.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 90 MPa Show Supplier Material materials with Resistencia a la flexión of 90 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 88 MPa Show Supplier Material materials with Resistencia a la tracción of 88 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 13 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 152 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 152 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 152 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 152 °C | ||
Temperatura de reblandecimiento Vicat | 173 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 173 °C | ISO 306 | Rate B/120 | |
Inflamabilidad | FAA Flammability, FAR 25.853 A/B: <5- FAR 25.853 <br> OSU peak heat release rate (5 minute test): 36kW/m² FAR 25.853 <br> Vertical Burn a (60s) passes at: 2sec FAR 25.853 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 8.9 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 8.9 g/10min | ASTM D 1238 | 295°C/6.6 kgf | |
Velocidad de flujo del volumen derretido | 40 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 40 cm³/10min | ISO 1133 | MVR at 340°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Fused Deposition Modeling (FDM), Electronics, Enclosures, Electronic Components, Air Cabin Interiors, Aircraft Seating, Aerospace, Audio, Displays, Document Handling, Composite, Non-LED Lighting, Photovoltaic Components, Wireless Communications | |
Availability | Europe,Asia,Americas | |
Processing methods | Melt Temperature: 330 to 350.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |