General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 1.75 % Show Supplier Material materials with Absorción de agua of 1.75 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.3 g/cm³ Show Supplier Material materials with Densidad of 1.3 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.3 [-] Show Supplier Material materials with Densidad relativa of 1.3 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.6 % Show Supplier Material materials with Moisture absorption of 0.6 % | ISO 62 | (23°C / 50% RH) |
Índice límite de óxigeno | 23.0 °C | 45 % Show Supplier Material materials with Índice límite de óxigeno of 45 % |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 50 % Show Supplier Material materials with Elongación of 50 % | ISO 527 | break, 5 mm/min | ||
Hardness, Ball Indentation | 23.0 °C | 140 MPa Show Supplier Material materials with Hardness, Ball Indentation of 140 MPa | ISO 2039-1 | H358/30 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 69 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 69 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, Total Energy | 23.0 °C | 33 J Show Supplier Material materials with Instrumented Impact, Total Energy of 33 J | ASTM D 3763 | 23°C | ||
Módulo de flexión | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo de flexión of 3.1 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo elástico of 3.1 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 123 MPa Show Supplier Material materials with Resistencia a la flexión of 123 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 78 MPa Show Supplier Material materials with Resistencia a la tracción of 78 MPa | ISO 527 | break, 5 mm/min | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | 80*10*4, -30°C | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Izod no entallado | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Passes | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coeficiente de dilatación térmica | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Conductividad térmica | 23.0 °C | 0.22 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.22 W/(m·K) | ASTM E 1530 | | ||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 237 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 237 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 228 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 228 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 228 - 237 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 228 - 237 °C | ||||
Temperatura de reblandecimiento Vicat | 238 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 238 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3.2mm IEC 60695-2-12 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 100 Hz | 23.0 °C | 3.41 [-] Show Supplier Material materials with Constante dieléctrica, 100 Hz of 3.41 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 8E-3 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 7E-3 [-] | IEC 60250 |
Dissipation factor, 1kHz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 1kHz of 1E-3 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 0.03 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 0.03 [-] | IEC 60250 | 50/60 Hz |
Rigidez dieléctrica | 23.0 °C | 17 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 17 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Índice de seguimiento comparativo | 23.0 °C | 175 V Show Supplier Material materials with Índice de seguimiento comparativo of 175 V | IEC 60112 | |
Óptico
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción transversal of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 15.5 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 15.5 g/10min | ASTM D 1238 | 367°C/6.6 kgf | |
Velocidad de flujo del volumen derretido | 8 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 8 cm³/10min | ISO 1133 | MVR at 360°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Vent Depth: 0.025 to 0.076mm | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |