General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad relativa | 23.0 °C | 1.4 [-] Show Supplier Material materials with Densidad relativa of 1.4 [-] | ASTM D 792 | |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 3 % Show Supplier Material materials with Elongación of 3 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 101 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 101 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 7.2 GPa Show Supplier Material materials with Módulo de flexión of 7.2 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Módulo elástico | 23.0 °C | 7 GPa Show Supplier Material materials with Módulo elástico of 7 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 206 MPa Show Supplier Material materials with Resistencia a la flexión of 206 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 151 MPa Show Supplier Material materials with Resistencia a la tracción of 151 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 101 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 101 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 211 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 211 °C | ASTM D 648 | 6.4 mm, unannealed | |
Temperatura de flexión bajo carga | 211 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 211 °C | ||
Inflamabilidad | OSU peak heat release rate (5 minute test): 40kW/m² FAR 25.853 <br> Vertical Burn b (12s) passes at: 0sec FAR 25.853 <br> NBS Smoke Density, Flaming, Ds 4 min: 5- ASTM E 662 <br> NBS Smoke Density, Flaming, Ds 1.5 min: 0- ASTM E 662 <br> NBS Smoke Density, Flaming, Dmax: 5- ASTM E 662 <br> Vertical Burn a (60s) passes at: 0sec FAR 25.853 <br> FAA Flammability, FAR 25.853 A/B: NATURAL- FAR 25.853 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.3 % Show Supplier Material materials with Contracción of 0.3 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 5.7 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 5.7 g/10min | ASTM D 1238 | 337°C/6.6 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Aerospace, Aircraft Seating, Air Cabin Interiors, Electronic Components | |
Availability | Asia,Americas | |
Processing methods | Nozzle Temperature: 360 to 380.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |