AA Standards Grade 5050 H24

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.69 g/cm³

Show Material materials with Density of 2.69 g/cm³

H24

AA Standards, ASTM B209

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H24

AA Standards, ASTM B209

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 5000 Series Aluminium

Shear modulus

26.0 - 26.5 GPa

Show Material materials with Shear modulus of 26.0 - 26.5 GPa

Typical for Wrought 5000 Series Aluminium

Tensile strength

170.0 - 215.0 MPa

Show Material materials with Tensile strength of 170.0 - 215.0 MPa

H24

AA Standards, ASTM B209

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

20 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H24

AA Standards, ASTM B209

100 °C

2.38e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K

H24

AA Standards, ASTM B209

Max service temperature

150.0 °C

Show Material materials with Max service temperature of 150.0 °C

Typical for Wrought 5000 Series Aluminium

Melting point

625.0 - 650.0 °C

Show Material materials with Melting point of 625.0 - 650.0 °C

H24

AA Standards, ASTM B209

Specific heat capacity

879.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K)

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

193 W/(m·K)

Show Material materials with Thermal conductivity of 193 W/(m·K)

H24

AA Standards, ASTM B209

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

29000000.0 S/m

Show Material materials with Electrical conductivity of 29000000.0 S/m

H24

AA Standards, ASTM B209

Electrical resistivity

3.45e-08 Ω·m

Show Material materials with Electrical resistivity of 3.45e-08 Ω·m

H24

AA Standards, ASTM B209

Chemical properties

PropertyValueConditionRelated Standards

Chromium

0.1 %

Show Material materials with Chromium of 0.1 %

H24

AA Standards, ASTM B209

Copper

0.2 %

Show Material materials with Copper of 0.2 %

H24

AA Standards, ASTM B209

Iron

0.70 %

Show Material materials with Iron of 0.70 %

H24

AA Standards, ASTM B209

Magnesium

1.1 - 1.8 %

Show Material materials with Magnesium of 1.1 - 1.8 %

H24

AA Standards, ASTM B209

Manganese

0.1 %

Show Material materials with Manganese of 0.1 %

H24

AA Standards, ASTM B209

Silicon

0.4 %

Show Material materials with Silicon of 0.4 %

H24

AA Standards, ASTM B209

Zinc

0.25 %

Show Material materials with Zinc of 0.25 %

H24

AA Standards, ASTM B209

Technological properties

Property
Brazing

general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O), poor (H32, H34), sufficient (H36, H38)

Workability

general (condition): good (O, H32), acceptable (H34), poor(H36, H38)