Properties
General
| Property | Value | Temperature |
|---|---|---|
Density | 2.68 - 2.69 g/cm³ Show Material materials with Density of 2.68 - 2.69 g/cm³ at 23.0 °C | 23.0 °C |
Mechanical
| Property | Value | Temperature | Comment |
|---|---|---|---|
Elastic modulus | 69 - 70 GPa Show Material materials with Elastic modulus of 69 - 70 GPa at 23.0 °C | 23.0 °C | |
Elongation A50 | 3 - 5 % Show Material materials with Elongation A50 of 3 - 5 % at 20.0 °C | 20.0 °C | |
3 - 5 % Show Material materials with Elongation A50 of 3 - 5 % at 23.0 °C | 23.0 °C | ||
Elongation A50, transverse | 3 - 5 % Show Material materials with Elongation A50, transverse of 3 - 5 % at 20.0 °C | 20.0 °C | |
Plane-Strain Fracture Toughnes | 22 - 35 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Shear modulus | 26 - 26.5 GPa Show Material materials with Shear modulus of 26 - 26.5 GPa at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Tensile strength | 170 - 215 MPa Show Material materials with Tensile strength of 170 - 215 MPa at 20.0 °C | 20.0 °C | |
170 - 215 MPa Show Material materials with Tensile strength of 170 - 215 MPa at 23.0 °C | 23.0 °C | ||
Tensile strength, transverse | 170 - 215 MPa Show Material materials with Tensile strength, transverse of 170 - 215 MPa at 20.0 °C | 20.0 °C | |
Yield strength Rp0.2 | 130 MPa Show Material materials with Yield strength Rp0.2 of 130 MPa at 20.0 °C | 20.0 °C | |
130 MPa Show Material materials with Yield strength Rp0.2 of 130 MPa at 23.0 °C | 23.0 °C | ||
Yield strength Rp0.2, transverse | 130 MPa Show Material materials with Yield strength Rp0.2, transverse of 130 MPa at 20.0 °C | 20.0 °C | |
Thermal
| Property | Value | Temperature | Comment |
|---|---|---|---|
Coefficient of thermal expansion | 2.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K at 20.0 °C | 20.0 °C | |
2.38E-5 1/K Show Material materials with Coefficient of thermal expansion of 2.38E-5 1/K at 100.0 °C | 100.0 °C | ||
Max service temperature | 150 °C Show Material materials with Max service temperature of 150 °C | Typical for Wrought 5000 Series Aluminium | |
Melting point | 620 - 650 °C Show Material materials with Melting point of 620 - 650 °C | ||
Specific heat capacity | 879 - 963 J/(kg·K) Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K) at 23.0 °C | 23.0 °C | Typical for Wrought 5000 Series Aluminium |
Thermal conductivity | 170 - 193 W/(m·K) Show Material materials with Thermal conductivity of 170 - 193 W/(m·K) at 23.0 °C | 23.0 °C | |
Electrical
| Property | Value | Temperature |
|---|---|---|
Electrical conductivity | 2.30E+7 - 2.90E+7 S/m Show Material materials with Electrical conductivity of 2.30E+7 - 2.90E+7 S/m at 23.0 °C | 23.0 °C |
Electrical resistivity | 3.45E-8 - 4.35E-8 Ω·m Show Material materials with Electrical resistivity of 3.45E-8 - 4.35E-8 Ω·m at 23.0 °C | 23.0 °C |
Chemical properties
| Property | ||
|---|---|---|
Chromium | 0.1 % | |
Copper | 0.2 % | |
Iron | 0.7 % | |
Magnesium | 1.1 - 1.8 % | |
Manganese | 0.1 % | |
Other | each 0.05, total 0.10, Rest Al | |
Silicon | 0.4 % | |
Zinc | 0.25 % |
Technological properties
| Property | ||
|---|---|---|
| Workability | Good workability. | |