Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Bending Fatigue Strength | 85.0 MPa Show Material materials with Bending Fatigue Strength of 85.0 MPa | O | AA Standards | ||
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Elongation A100 | 23.0 °C | 18 % Show Material materials with Elongation A100 of 18 % | |||
Elongation A50 | 23.0 °C | 15 - 24 % Show Material materials with Elongation A50 of 15 - 24 % | |||
Hardness, Brinell | 36.0 [-] Show Material materials with Hardness, Brinell of 36.0 [-] | O | AA Standards | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | |||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | |||
Tensile strength | 145.0 MPa Show Material materials with Tensile strength of 145.0 MPa | O | AA Standards | ||
125.0 - 165.0 MPa Show Material materials with Tensile strength of 125.0 - 165.0 MPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547 | |||
125.0 MPa Show Material materials with Tensile strength of 125.0 MPa | O | AA Standards, ASTM B483 | |||
Yield strength Rp0.2 | 23.0 °C | 40 - 55 MPa Show Material materials with Yield strength Rp0.2 of 40 - 55 MPa | |||
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 100 °C, 20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | |
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 625.0 - 650.0 °C Show Material materials with Melting point of 625.0 - 650.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 193 W/(m·K) Show Material materials with Thermal conductivity of 193 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 29000000.0 S/m Show Material materials with Electrical conductivity of 29000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Electrical resistivity | 3.45e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 |
Chemical properties
| Property | Value | Condition | Related Standards | ||
|---|---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Copper | 0.2 % Show Material materials with Copper of 0.2 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Iron | 0.70 % Show Material materials with Iron of 0.70 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Magnesium | 1.1 - 1.8 % Show Material materials with Magnesium of 1.1 - 1.8 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Manganese | 0.1 % Show Material materials with Manganese of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Other | each 0.05, total 0.15, Rest Al | ||||
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 | ||
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O), poor (H32, H34), sufficient (H36, H38) | |
| Workability | general (condition): good (O, H32), acceptable (H34), poor(H36, H38) | |