EN 573-3 Grade AW-5059 H112

Want to keep this datasheet? Save it now in your required format

Description

Material EN AW-Al Mg5,5MnZnZr is produced for sheet metals, strip and plates, for forged parts and prematerial as well as for wire and prewire. The material is food-safe.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.66 g/cm³

Show Material materials with Density of 2.66 g/cm³ at 23.0 °C

23.0 °C

Mechanical

PropertyValueTemperatureComment

Bending angle 180°

2 - 4 °/t

Show Material materials with Bending angle 180° of 2 - 4 °/t at 23.0 °C

23.0 °C

Elastic modulus

69 - 70 GPa

Show Material materials with Elastic modulus of 69 - 70 GPa at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Elongation

20 %

Show Material materials with Elongation of 20 % at 20.0 °C

20.0 °C

Elongation A100

20 - 22 %

Show Material materials with Elongation A100 of 20 - 22 % at 23.0 °C

23.0 °C

Elongation A50

20 - 24 %

Show Material materials with Elongation A50 of 20 - 24 % at 20.0 °C

20.0 °C

20 %

Show Material materials with Elongation A50 of 20 % at 23.0 °C

23.0 °C

Elongation A50, transverse

20 %

Show Material materials with Elongation A50, transverse of 20 % at 20.0 °C

20.0 °C

Elongation, transverse

20 %

Show Material materials with Elongation, transverse of 20 % at 20.0 °C

20.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Shear modulus

26 - 26.5 GPa

Show Material materials with Shear modulus of 26 - 26.5 GPa at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Tensile strength

330 - 380 MPa

Show Material materials with Tensile strength of 330 - 380 MPa at 20.0 °C

20.0 °C

330 - 380 MPa

Show Material materials with Tensile strength of 330 - 380 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Tensile strength, transverse

330 - 380 MPa

Show Material materials with Tensile strength, transverse of 330 - 380 MPa at 20.0 °C

20.0 °C

Yield strength Rp0.2

160 MPa

Show Material materials with Yield strength Rp0.2 of 160 MPa at 20.0 °C

20.0 °C

160 MPa

Show Material materials with Yield strength Rp0.2 of 160 MPa at 23.0 °C

23.0 °C

Unlock all property charts

Yield strength Rp0.2, transverse

160 MPa

Show Material materials with Yield strength Rp0.2, transverse of 160 MPa at 20.0 °C

20.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.2E-5 - 2.5E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.5E-5 1/K at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Max service temperature

150 °C

Show Material materials with Max service temperature of 150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

560 - 655 °C

Show Material materials with Melting point of 560 - 655 °C

Typical for Wrought 5000 Series Aluminium

Specific heat capacity

879 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 879 - 963 J/(kg·K) at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Thermal conductivity

112 - 205 W/(m·K)

Show Material materials with Thermal conductivity of 112 - 205 W/(m·K) at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Electrical

PropertyValueTemperatureComment

Electrical conductivity

1.80E+7 - 3.10E+7 S/m

Show Material materials with Electrical conductivity of 1.80E+7 - 3.10E+7 S/m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Electrical resistivity

3.3E-8 - 5E-8 Ω·m

Show Material materials with Electrical resistivity of 3.3E-8 - 5E-8 Ω·m at 23.0 °C

23.0 °C

Typical for Wrought 5000 Series Aluminium

Chemical properties

Property

Chromium

0.25 - 0.3 %

Copper

0.25 %

Iron

0.5 %

Magnesium

3.5 - 6 %

Manganese

0.4 - 1.2 %

Other

each 0.05, total 0.15, Rest Al

Silicon

0.45 %

Titanium

0.15 - 0.2 %

Zinc

0.4 - 0.9 %

Zirconium

0.05 - 0.25 %

Technological properties

Property
Workability

Good workability.