Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.66 g/cm³ Show Material materials with Density of 2.66 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 71.0 GPa Show Material materials with Elastic modulus of 71.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 250.0 MPa Show Material materials with Tensile strength of 250.0 MPa | O | AA Standards, ASTM B209 | |
255.0 MPa Show Material materials with Tensile strength of 255.0 MPa | O | AA Standards, ASTM B209 | ||
260.0 MPa Show Material materials with Tensile strength of 260.0 MPa | O | AA Standards, ASTM B209 | ||
270.0 - 345.0 MPa Show Material materials with Tensile strength of 270.0 - 345.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||
270.0 - 350.0 MPa Show Material materials with Tensile strength of 270.0 - 350.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345 | ||
275.0 - 350.0 MPa Show Material materials with Tensile strength of 275.0 - 350.0 MPa | O | AA Standards, ASTM B209, ASTM B547 | ||
290.0 MPa Show Material materials with Tensile strength of 290.0 MPa | O | AA Standards |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | |
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 580.0 - 640.0 °C Show Material materials with Melting point of 580.0 - 640.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 117.0 Show Material materials with Thermal conductivity of 117.0 | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 17000000.0 S/m Show Material materials with Electrical conductivity of 17000000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Electrical resistivity | 5.88e-08 Ω·m Show Material materials with Electrical resistivity of 5.88e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Chromium | 0.05 - 0.25 % Show Material materials with Chromium of 0.05 - 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Copper | 0.1 % Show Material materials with Copper of 0.1 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Magnesium | 4.0 - 4.9 % Show Material materials with Magnesium of 4.0 - 4.9 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Silicon | 0.4 % Show Material materials with Silicon of 0.4 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Titanium | 0.15 % Show Material materials with Titanium of 0.15 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | O | AA Standards, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B547 |
Technological properties
Property | ||
---|---|---|
Brazing | general: no brazing is known or developed | |
Corrosion properties | Stress corrosion cracking: kein Schadensfall im Betrieb und bei Labortests (O, H321, H116), kein Schadensfall im Betrieb, eingeschränkte Schäden bei den Labortests (H111), general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor | |
Workability | general (condition): acceptable (O), poor(H321, H116, H111) |