EN 573-1 Grade AW-5454 H38

Want to keep this datasheet? Save it now in your required format

Description

Excellent corrosion resistance and surface finishing properties.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-1 Grade AW-5454 H38 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.68 - 2.69 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

0.2 - 3 mm

Mechanical

Elastic modulus

E

70 - 70.5 GPa at 20 °C

Show 5000 Series materials with Elastic modulus of 70 - 70.5 GPa at 20 °C

Elongation A100

A100

3 % at 20 °C

Show 5000 Series materials with Elongation A100 of 3 % at 20 °C

Elongation A50

A50

3 % at 20 °C

Show 5000 Series materials with Elongation A50 of 3 % at 20 °C

Elongation A50, transverse

A50,trans

3 % at 20 °C

Show 5000 Series materials with Elongation A50, transverse of 3 % at 20 °C

Hardness, Brinell

HB

93 [-] at 20 °C

Show 5000 Series materials with Hardness, Brinell of 93 [-] at 20 °C

Hardness, HBW

HBW

93 [-] at 20 °C

Show 5000 Series materials with Hardness, HBW of 93 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 5000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 5000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 5000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

26.5 - 27 GPa at 20 °C

Show 5000 Series materials with Shear modulus of 26.5 - 27 GPa at 20 °C

Tensile strength

Rm

310 MPa at 20 °C

Show 5000 Series materials with Tensile strength of 310 MPa at 20 °C

Tensile strength, transverse

Rm,trans

310 MPa at 20 °C

Show 5000 Series materials with Tensile strength, transverse of 310 MPa at 20 °C

Yield strength

YS

250 MPa at 20 °C

Show 5000 Series materials with Yield strength of 250 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

250 - 280 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2 of 250 - 280 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

250 MPa at 20 °C

Show 5000 Series materials with Yield strength Rp0.2, transverse of 250 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.19E-5 1/K at -50 °C

20-100°C

Hide chart

Max service temperature

Tmax

150 °C

Typical for Wrought 5000 Series Aluminium

Melting point

Tm

602 - 646 °C

Specific heat capacity

cp

897 - 900 J/(kg·K) at 20 °C

Thermal conductivity

λ

130 - 150 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

1.90E+7 - 2.10E+7 S/m at 20 °C

Electrical resistivity

ρel

4.76E-8 - 5.26E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Mg

2.4 - 3 %

Mn

0.5 - 1 %

Fe

0.4 %

Si

0.25 %

Zn

0.25 %

More

Technological properties

Anodizing

Excellent

Application areas

Vessels: Pressure; Components: General transportation

Brazing

Brazing is not recommended.

Corrosion properties

Excellent

General machinability

Fair

Surface Finish

Mill finish.

Welding

Very Good

Workability

Good

This material data has been provided by Aludium,WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.