General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.69 g/cm³ Show Material materials with Density of 2.69 g/cm³ | H24 | AA Standards, ASTM B209 |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H24 | AA Standards, ASTM B209 | |
Hardness, Brinell | 40.0 [-] Show Material materials with Hardness, Brinell of 40.0 [-] | H24 | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 5000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 5000 Series Aluminium | ||
Shear modulus | 26.0 - 26.5 GPa Show Material materials with Shear modulus of 26.0 - 26.5 GPa | Typical for Wrought 5000 Series Aluminium | ||
Tensile strength | 125.0 - 180.0 MPa Show Material materials with Tensile strength of 125.0 - 180.0 MPa | H24 | AA Standards, ASTM B209 | |
160.0 MPa Show Material materials with Tensile strength of 160.0 MPa | H24 | AA Standards |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H24 | AA Standards, ASTM B209 | |
100 °C | 2.38e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.38e-05 1/K | H24 | AA Standards, ASTM B209 | ||
Max service temperature | 150.0 °C Show Material materials with Max service temperature of 150.0 °C | Typical for Wrought 5000 Series Aluminium | |||
Melting point | 635.0 - 655.0 °C Show Material materials with Melting point of 635.0 - 655.0 °C | H24 | AA Standards, ASTM B209 | ||
Specific heat capacity | 879.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 879.0 - 963.0 J/(kg·K) | Typical for Wrought 5000 Series Aluminium | |||
Thermal conductivity | 205 W/(m·K) Show Material materials with Thermal conductivity of 205 W/(m·K) | H24 | AA Standards, ASTM B209 |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 31000000.0 S/m Show Material materials with Electrical conductivity of 31000000.0 S/m | H24 | AA Standards, ASTM B209 |
Electrical resistivity | 3.23e-08 Ω·m Show Material materials with Electrical resistivity of 3.23e-08 Ω·m | H24 | AA Standards, ASTM B209 |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Copper | 0.1 % Show Material materials with Copper of 0.1 % | H24 | AA Standards, ASTM B209 |
Gallium | 0.03 % Show Material materials with Gallium of 0.03 % | H24 | AA Standards, ASTM B209 |
Iron | 0.10 % Show Material materials with Iron of 0.10 % | H24 | AA Standards, ASTM B209 |
Magnesium | 0.6 - 1.0 % Show Material materials with Magnesium of 0.6 - 1.0 % | H24 | AA Standards, ASTM B209 |
Manganese | 0.03 % Show Material materials with Manganese of 0.03 % | H24 | AA Standards, ASTM B209 |
Silicon | 0.08 % Show Material materials with Silicon of 0.08 % | H24 | AA Standards, ASTM B209 |
Vanadium | 0.05 % Show Material materials with Vanadium of 0.05 % | H24 | AA Standards, ASTM B209 |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | H24 | AA Standards, ASTM B209 |
Technological properties
Property | ||
---|---|---|
Brazing | general: Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: poor (H241, H25, H26, H28) | |
Workability | general (condition): good (H241), acceptable (H25, H26), poor(H28) |