EN 573-3 Grade AW-1350 H111

Want to keep this datasheet? Save it now in your required format

Description

Excellent electrical conductivity.

Related Standards

Equivalent Materials

This material data has been provided by AluKey,Aludium.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueTemperature

Density

2.69 - 2.71 g/cm³

Show Material materials with Density of 2.69 - 2.71 g/cm³ at 23.0 °C

23.0 °C

Dimension

PropertyValue

Thickness

0.2 - 3 mm

Show Material materials with Thickness of 0.2 - 3 mm

Mechanical

PropertyValueTemperatureComment

Bending angle 180°

0 - 1 °/t

Show Material materials with Bending angle 180° of 0 - 1 °/t at 23.0 °C

23.0 °C

Bending angle 90°

0 - 1 °/t

Show Material materials with Bending angle 90° of 0 - 1 °/t at 23.0 °C

23.0 °C

Elastic modulus

69 - 70 GPa

Show Material materials with Elastic modulus of 69 - 70 GPa at 23.0 °C

23.0 °C

Elongation

32 %

Show Material materials with Elongation of 32 % at 23.0 °C

23.0 °C

Elongation A100

32 %

Show Material materials with Elongation A100 of 32 % at 23.0 °C

23.0 °C

Elongation A50

20 - 35 %

Show Material materials with Elongation A50 of 20 - 35 % at 23.0 °C

23.0 °C

Hardness, Brinell

20 [-]

Show Material materials with Hardness, Brinell of 20 [-] at 23.0 °C

23.0 °C

Plane-Strain Fracture Toughnes

22 - 35 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-] at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus

26.5 GPa

Show Material materials with Shear modulus of 26.5 GPa at 23.0 °C

23.0 °C

Tensile strength

65 - 105 MPa

Show Material materials with Tensile strength of 65 - 105 MPa at 23.0 °C

23.0 °C

Yield strength Rp0.2

20 MPa

Show Material materials with Yield strength Rp0.2 of 20 MPa at 23.0 °C

23.0 °C

Thermal

PropertyValueTemperatureComment

Coefficient of thermal expansion

2.36E-5 - 2.38E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 - 2.38E-5 1/K at 20.0 °C

20.0 °C

20-100°C

2.36E-5 - 2.4E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.36E-5 - 2.4E-5 1/K at 100.0 °C

100.0 °C

20-100°C

Melting point

645 - 657 °C

Show Material materials with Melting point of 645 - 657 °C

Specific heat capacity

900 - 963 J/(kg·K)

Show Material materials with Specific heat capacity of 900 - 963 J/(kg·K) at 23.0 °C

23.0 °C

Typical for Wrought 1000 Series Aluminium

Thermal conductivity

138 - 235 W/(m·K)

Show Material materials with Thermal conductivity of 138 - 235 W/(m·K) at 23.0 °C

23.0 °C

Electrical

PropertyValueTemperature

Electrical conductivity

3.54E+7 - 3.65E+7 S/m

Show Material materials with Electrical conductivity of 3.54E+7 - 3.65E+7 S/m at 23.0 °C

23.0 °C

Electrical resistivity

2.74E-8 - 4.9E-8 Ω·m

Show Material materials with Electrical resistivity of 2.74E-8 - 4.9E-8 Ω·m at 23.0 °C

23.0 °C

Chemical properties

Property

Aluminium

99.5 %

Boron

0.05 %

Chromium

0.01 %

Copper

0.05 %

Gallium

0.03 %

Iron

0.4 %

Manganese

0.01 %

Other

0.1 %

Ti + V < 0.02, each 0.03, total 0.10

Silicon

0.1 %

Zinc

0.05 %

Technological properties

Property
Anodizing

Good (For surface protection only)

Application areas

Conductors; rods for the manufacture of aluminium conductor wires.

Brazing

Excellent

Corrosion properties

Very Good

Welding

Very Good

Workability

Very Good