EN 573-1 Grade AW-1350 H12

Want to keep this datasheet? Save it now in your required format

Description

Excellent electrical conductivity.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-1 Grade AW-1350 H12 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.69 - 2.71 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

0.2 - 3 mm

Mechanical

Bending angle 180°

θ180

0.5 - 1 °/t at 20 °C

Show 1000 Series materials with Bending angle 180° of 0.5 - 1 °/t at 20 °C

Bending angle 90°

θ90

0 - 3 °/t at 20 °C

Show 1000 Series materials with Bending angle 90° of 0 - 3 °/t at 20 °C

Elastic modulus

E

69 - 70 GPa at 20 °C

Show 1000 Series materials with Elastic modulus of 69 - 70 GPa at 20 °C

Elongation

A

9 % at 20 °C

Show 1000 Series materials with Elongation of 9 % at 20 °C

Elongation A50

A50

2 - 20 % at 20 °C

Show 1000 Series materials with Elongation A50 of 2 - 20 % at 20 °C

Hardness, Brinell

HB

28 [-] at 20 °C

Show 1000 Series materials with Hardness, Brinell of 28 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 1000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 1000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 1000 Series Aluminium

Shear modulus

G

26.5 GPa at 20 °C

Show 1000 Series materials with Shear modulus of 26.5 GPa at 20 °C

Tensile strength

Rm

85 - 125 MPa at 20 °C

Show 1000 Series materials with Tensile strength of 85 - 125 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

65 MPa at 20 °C

Show 1000 Series materials with Yield strength Rp0.2 of 65 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.36E-5 - 2.38E-5 1/K at 20 °C

20-100°C

Hide chart

Melting point

Tm

645 - 657 °C

Specific heat capacity

cp

900 - 963 J/(kg·K) at 20 °C

Typical for Wrought 1000 Series Aluminium

Thermal conductivity

λ

138 - 235 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

3.54E+7 - 3.65E+7 S/m at 20 °C

Electrical resistivity

ρel

2.74E-8 - 4.9E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Al

99.5 %

Fe

0.4 %

Other

0.1 %

Ti + V < 0.02, each 0.03, total 0.10

Si

0.1 %

B

0.05 %

More

Technological properties

Anodizing

Good (For surface protection only)

Application areas

Conductors; rods for the manufacture of aluminium conductor wires.

Brazing

Excellent

Corrosion properties

Very Good

Welding

Very Good

Workability

Very Good

This material data has been provided by Aludium,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.