General
Property | Value | Condition | Related Standards |
---|---|---|---|
Density | 2.705 g/cm³ Show Material materials with Density of 2.705 g/cm³ | O | AA Standards |
Mechanical
Property | Value | Condition | Related Standards | Comment |
---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | O | AA Standards | |
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 1000 Series Aluminium | ||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 1000 Series Aluminium | ||
Shear modulus | 25.9 GPa Show Material materials with Shear modulus of 25.9 GPa | Typical for Wrought 1000 Series Aluminium | ||
Tensile strength | 85.0 MPa Show Material materials with Tensile strength of 85.0 MPa | O | AA Standards |
Thermal
Property | Temperature | Value | Condition | Related Standards | Comment |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards | |
100 °C | 2.36e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K | O | AA Standards | ||
Melting point | 645.0 - 655.0 °C Show Material materials with Melting point of 645.0 - 655.0 °C | O | AA Standards | ||
Specific heat capacity | 900.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K) | Typical for Wrought 1000 Series Aluminium | |||
Thermal conductivity | 234 W/(m·K) Show Material materials with Thermal conductivity of 234 W/(m·K) | O | AA Standards |
Electrical
Property | Value | Condition | Related Standards |
---|---|---|---|
Electrical conductivity | 36000000.0 S/m Show Material materials with Electrical conductivity of 36000000.0 S/m | O | AA Standards |
Electrical resistivity | 2.78e-08 Ω·m Show Material materials with Electrical resistivity of 2.78e-08 Ω·m | O | AA Standards |
Chemical properties
Property | Value | Condition | Related Standards |
---|---|---|---|
Aluminium | 99.5 % Show Material materials with Aluminium of 99.5 % | O | AA Standards |
Boron | 0.05 % Show Material materials with Boron of 0.05 % | O | AA Standards |
Chromium | 0.01 % Show Material materials with Chromium of 0.01 % | O | AA Standards |
Copper | 0.05 % Show Material materials with Copper of 0.05 % | O | AA Standards |
Gallium | 0.03 % Show Material materials with Gallium of 0.03 % | O | AA Standards |
Iron | 0.40 % Show Material materials with Iron of 0.40 % | O | AA Standards |
Manganese | 0.01 % Show Material materials with Manganese of 0.01 % | O | AA Standards |
Silicon | 0.1 % Show Material materials with Silicon of 0.1 % | O | AA Standards |
Zinc | 0.05 % Show Material materials with Zinc of 0.05 % | O | AA Standards |
Technological properties
Property | ||
---|---|---|
Brazing | general: possible with commercial processes and methods | |
Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
General machinability | General: not suitable (O, H12, H111), poor (H14, H24, H16, H26, H18) | |
Workability | general (condition): good (O, H12, H111, H14, H24), acceptable (H16, H26, H18) |