General
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Elastic modulus | 72.5 GPa Show Material materials with Elastic modulus of 72.5 GPa | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 65.0 - 73.5 GPa Show Material materials with Elastic modulus of 65.0 - 73.5 GPa | H18 | EN 573-3 | Wire | ||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 2000 Series Aluminium | ||||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 2000 Series Aluminium | ||||
Shear modulus | 27.2 GPa Show Material materials with Shear modulus of 27.2 GPa | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 26.0 - 28.5 GPa Show Material materials with Shear modulus of 26.0 - 28.5 GPa | H18 | EN 573-3 | Wire | ||
Tensile strength | 315.0 MPa Show Material materials with Tensile strength of 315.0 MPa | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | ||
20.0 °C | 315.0 MPa Show Material materials with Tensile strength of 315.0 MPa | H18 | EN 573-3 | Wire |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar |
100 °C | 2.3e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3e-05 1/K | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
Melting point | 512.0 - 650.0 °C Show Material materials with Melting point of 512.0 - 650.0 °C | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
Specific heat capacity | 20.0 °C | 921.0 J/(kg·K) Show Material materials with Specific heat capacity of 921.0 J/(kg·K) | H18 | EN 573-3 | Wire |
Thermal conductivity | 20.0 °C | 130.0 - 200.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 200.0 W/(m·K) | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 18000000.0 - 28000000.0 S/m Show Material materials with Electrical conductivity of 18000000.0 - 28000000.0 S/m | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Electrical resistivity | 3.57e-08 - 5.56e-08 Ω·m Show Material materials with Electrical resistivity of 3.57e-08 - 5.56e-08 Ω·m | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Chromium | 0.1 % Show Material materials with Chromium of 0.1 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Copper | 3.5 - 4.5 % Show Material materials with Copper of 3.5 - 4.5 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Iron | 0.7 % Show Material materials with Iron of 0.7 % | H18 | EN 573-3 | Wire |
0.70 % Show Material materials with Iron of 0.70 % | H18 | EN 573-3, EN 1301 | Strip, Sheet, Plate, Tube, Bar | |
Magnesium | 0.4 - 1.0 % Show Material materials with Magnesium of 0.4 - 1.0 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Manganese | 0.4 - 1.0 % Show Material materials with Manganese of 0.4 - 1.0 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Silicon | 0.2 - 0.8 % Show Material materials with Silicon of 0.2 - 0.8 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Zinc | 0.25 % Show Material materials with Zinc of 0.25 % | H18 | EN 573-3, EN 1301 | Wire, Strip, Sheet, Plate, Tube, Bar |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not suitable, Protective: good | |
Brazing | hard brazing (with flux/ without flux): not suitable / not suitable, friction soldering: acceptable, soft brazing with flux: not suitable | |
Corrosion properties | Seawater: poor, weathering: sufficient | |
Workability | Bending / Spinning (cold): good / acceptable, Impact extrusion (cold): acceptable, Deep drawing / upsetting (Condition) acceptable (O) / acceptable (O) |