EN 573-3 Grade AW-3103 H36

Want to keep this datasheet? Save it now in your required format

Description

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-3 Grade AW-3103 H36 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.73 g/cm³ at 20 °C

Dimension

Dimensions

Durchmesser

Mechanical

Elastic modulus

E

69.5 GPa at 20 °C

Show 3000 Series materials with Elastic modulus of 69.5 GPa at 20 °C

Elongation A100

A100

3 % at 20 °C

Show 3000 Series materials with Elongation A100 of 3 % at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 3000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 3000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus

G

26.1 GPa at 20 °C

Show 3000 Series materials with Shear modulus of 26.1 GPa at 20 °C

Tensile strength

Rm

170 MPa at 20 °C

Show 3000 Series materials with Tensile strength of 170 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

150 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2 of 150 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.35E-5 1/K at 20 °C

Hide chart

Melting point

Tm

645 - 655 °C

Specific heat capacity

cp

893 J/(kg·K) at 20 °C

Thermal conductivity

λ

160 - 200 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.20E+7 - 2.80E+7 S/m at 20 °C

Electrical resistivity

ρel

3.57E-8 - 4.55E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

Ti + Zr < 0.10, each 0.05, total 0.15, Rest Al

Mn

0.9 - 1.5 %

Fe

0.7 %

Si

0.5 %

Mg

0.3 %

More

Technological properties

Anodizing

decorative: sufficient, Protective: very good

Brazing

hard brazing (with flux/ without flux): very good to good / very good, friction soldering: very good, soft brazing with flux: very good

Corrosion properties

Seawater: good, weathering: very good

Workability

Bending / Spinning (cold): very good / very good, Impact extrusion (cold): good, Deep drawing / upsetting (Condition) very good (O) / very good (H12)

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.