EN 573-1 Grade AW-3103 H19

Want to keep this datasheet? Save it now in your required format

Description

Stronger and harder than 1200, yet retains comparable ductility and corrosion resistance.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-1 Grade AW-3103 H19 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.73 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

0.04 - 0.2 mm

Mechanical

Elastic modulus

E

70 GPa at -270 °C

Show 3000 Series materials with Elastic modulus of 70 GPa at -270 °C

Hide chart

Elongation A100

A100

0.5 % at 20 °C

Show 3000 Series materials with Elongation A100 of 0.5 % at 20 °C

Elongation A50

A50

0.5 - 2 % at 20 °C

Show 3000 Series materials with Elongation A50 of 0.5 - 2 % at 20 °C

Elongation A50, transverse

A50,trans

1 - 2 % at 20 °C

Show 3000 Series materials with Elongation A50, transverse of 1 - 2 % at 20 °C

Hardness, Brinell

HB

62 [-] at 20 °C

Show 3000 Series materials with Hardness, Brinell of 62 [-] at 20 °C

Hardness, HBW

HBW

58 [-] at 20 °C

Show 3000 Series materials with Hardness, HBW of 58 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 3000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 3000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Shear modulus

G

24 - 26.5 GPa at 20 °C

Show 3000 Series materials with Shear modulus of 24 - 26.5 GPa at 20 °C

Tensile strength

Rm

200 - 210 MPa at 20 °C

Show 3000 Series materials with Tensile strength of 200 - 210 MPa at 20 °C

Tensile strength, transverse

Rm,trans

200 MPa at 20 °C

Show 3000 Series materials with Tensile strength, transverse of 200 MPa at 20 °C

Yield strength

YS

175 MPa at 20 °C

Show 3000 Series materials with Yield strength of 175 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

175 - 180 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2 of 175 - 180 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

175 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2, transverse of 175 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.35E-5 1/K at 20 °C

20-100°C

Unlock all property charts

Melting point

Tm

645 - 655 °C

Specific heat capacity

cp

892 - 893 J/(kg·K) at 20 °C

Thermal conductivity

λ

160 - 200 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.20E+7 - 2.90E+7 S/m at 20 °C

Electrical resistivity

ρel

3.4E-8 - 4.55E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

Ti + Zr < 0.10, each 0.05, total 0.15, Rest Al

Mn

0.9 - 1.5 %

Fe

0.7 %

Si

0.5 %

Mg

0.3 %

More

Technological properties

Anodizing

Very Good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Sun Protection Systems: Single sheet (covering, sun breakers and gutters); Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels, Decoration; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Anodizing Quality; Lithography; Heat exchangers: Fins, Heat exchangers; Tubes: Flexible tube, Pipes; Cosmetics: Cosmetics pieces; Semi-rigid and corrugated: Smooth wall; Components: Automotive fins, Heat exchangers

Brazing

Excellent

Corrosion properties

Very Good

Welding

Very Good

Workability

Very Good

This material data has been provided by Aludium,WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.