EN 573-1 Grade AW-3105 H19

Want to keep this datasheet? Save it now in your required format

Description

A low to medium strength alloy with good corrosion resistance.

Related Standards

Equivalent Materials

Ashby charts

See where EN 573-1 Grade AW-3105 H19 falls on the material property chart for Density against Elastic modulus in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

Density

ρ

2.71 - 2.72 g/cm³ at 20 °C

Dimension

Dimensions

Dicke

Thickness

t

0.2 - 2 mm

Mechanical

Bending angle 180°

θ180

0 °/t at 20 °C

Show 3000 Series materials with Bending angle 180° of 0 °/t at 20 °C

Elastic modulus

E

69 - 70 GPa at 20 °C

Show 3000 Series materials with Elastic modulus of 69 - 70 GPa at 20 °C

Elongation A50

A50

1 % at 20 °C

Show 3000 Series materials with Elongation A50 of 1 % at 20 °C

Elongation A50, transverse

A50,trans

1 % at 20 °C

Show 3000 Series materials with Elongation A50, transverse of 1 % at 20 °C

Hardness, Brinell

HB

67 [-] at 20 °C

Show 3000 Series materials with Hardness, Brinell of 67 [-] at 20 °C

Hardness, HBW

HBW

67 [-] at 20 °C

Show 3000 Series materials with Hardness, HBW of 67 [-] at 20 °C

Plane-Strain Fracture Toughnes

KIC

22 - 35 MPa·√m at 20 °C

Show 3000 Series materials with Plane-Strain Fracture Toughnes of 22 - 35 MPa·√m at 20 °C

Typical for Wrought 3000 Series Aluminium

Poisson's ratio

ν

0.33 [-] at 20 °C

Show 3000 Series materials with Poisson's ratio of 0.33 [-] at 20 °C

Typical for Wrought 3000 Series Aluminium

Shear modulus

G

26 GPa at 20 °C

Show 3000 Series materials with Shear modulus of 26 GPa at 20 °C

Tensile strength

Rm

215 MPa at 20 °C

Show 3000 Series materials with Tensile strength of 215 MPa at 20 °C

Tensile strength, transverse

Rm,trans

215 MPa at 20 °C

Show 3000 Series materials with Tensile strength, transverse of 215 MPa at 20 °C

Yield strength

YS

190 MPa at 20 °C

Show 3000 Series materials with Yield strength of 190 MPa at 20 °C

Yield strength Rp0.2

Rp0.2

190 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2 of 190 MPa at 20 °C

Yield strength Rp0.2, transverse

Rp0.2,trans

190 MPa at 20 °C

Show 3000 Series materials with Yield strength Rp0.2, transverse of 190 MPa at 20 °C

Thermal

Coefficient of thermal expansion

α

2.36E-5 1/K at 20 °C

20-100°C

Hide chart

Melting point

Tm

635 - 655 °C

Specific heat capacity

cp

893 - 920 J/(kg·K) at 20 °C

Typical for Wrought 3000 Series Aluminium

Thermal conductivity

λ

160 - 190 W/(m·K) at 20 °C

Electrical

Electrical conductivity

σel

2.30E+7 - 2.70E+7 S/m at 20 °C

Electrical resistivity

ρel

3.8E-8 - 4.35E-8 Ω·m at 20 °C

Chemical properties

Element

Weight %

Comment

Other

-

each 0.05, total 0.15, Rest Al

Fe

0.7 %

Si

0.6 %

Zn

0.4 %

Cu

0.3 %

More

Technological properties

Anodizing

Good

Application areas

Facades: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Roofing: Single sheet, Sheets for composites/ sandwich Panels; Doors: Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Interiors and ceilings: Single sheet, Sheets for composites/ sandwich Panels, Sheets for mechanized panels; Furniture, Plinths, Blinds: Single sheet, Intermediate transformation/interior use; Heat exchangers: Fins; Closures: Short cups; Semi-rigid and corrugated: Pet food

Brazing

Good

Corrosion properties

Very Good

Surface Finish

Mill finish

Welding

Very Good

Workability

Very Good

This material data has been provided by Aludium,WIAM,AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.