General
Property | Value | Comment |
---|---|---|
Density | 2.65 - 2.7 g/cm³ Show Material materials with Density of 2.65 - 2.7 g/cm³ | Typical for Cast 3xx.x Series Aluminium |
Mechanical
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Bending Fatigue Strength | 60.0 - 90.0 MPa Show Material materials with Bending Fatigue Strength of 60.0 - 90.0 MPa | T6 | EN 1706 | Casting | ||
Elastic modulus | 73.0 - 80.0 GPa Show Material materials with Elastic modulus of 73.0 - 80.0 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Hardness, Brinell | 105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | T6 | EN 1706 | Casting | ||
20.0 °C | 105.0 [-] Show Material materials with Hardness, Brinell of 105.0 [-] | T6 | EN 1706 | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Cast 3xx.x Series Aluminium | ||||
Shear modulus | 2.8 GPa Show Material materials with Shear modulus of 2.8 GPa | Typical for Cast 3xx.x Series Aluminium | ||||
Tensile strength | 275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | T6 | EN 1706 | Casting | ||
20.0 °C | 275.0 MPa Show Material materials with Tensile strength of 275.0 MPa | T6 | EN 1706 |
Thermal
Property | Temperature | Value | Condition | Related Standards | Shape | Comment |
---|---|---|---|---|---|---|
Coefficient of thermal expansion | 20 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | T6 | EN 1706 | Casting | |
100.0 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | T6 | EN 1706 | Casting | ||
100 °C | 2.1e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.1e-05 1/K | T6 | EN 1706 | Casting | ||
Melting point | 505.0 - 770.0 °C Show Material materials with Melting point of 505.0 - 770.0 °C | Typical for Cast 3xx.x Series Aluminium | ||||
Specific heat capacity | 960.0 - 963.0 J/(kg·K) Show Material materials with Specific heat capacity of 960.0 - 963.0 J/(kg·K) | Typical for Cast 3xx.x Series Aluminium | ||||
Thermal conductivity | 20.0 °C | 130.0 - 150.0 W/(m·K) Show Material materials with Thermal conductivity of 130.0 - 150.0 W/(m·K) | T6 | EN 1706 | Casting |
Electrical
Property | Temperature | Value | Condition | Related Standards | Shape |
---|---|---|---|---|---|
Electrical conductivity | 20.0 °C | 16000000.0 - 22000000.0 S/m Show Material materials with Electrical conductivity of 16000000.0 - 22000000.0 S/m | T6 | EN 1706 | Casting |
Electrical resistivity | 4.55e-08 - 6.25e-08 Ω·m Show Material materials with Electrical resistivity of 4.55e-08 - 6.25e-08 Ω·m | T6 | EN 1706 | Casting |
Chemical properties
Property | Value | Condition | Related Standards | Shape |
---|---|---|---|---|
Aluminium | 85.35 % Show Material materials with Aluminium of 85.35 % | T6 | EN 1706 | |
Copper | 0.8 - 1.3 % Show Material materials with Copper of 0.8 - 1.3 % | T6 | EN 1706 | Casting |
Iron | 0.8 % Show Material materials with Iron of 0.8 % | T6 | EN 1706 | |
0.80 % Show Material materials with Iron of 0.80 % | T6 | EN 1706 | Casting | |
Lead | 0.1 % Show Material materials with Lead of 0.1 % | T6 | EN 1706 | Casting |
Magnesium | 0.25 - 0.65 % Show Material materials with Magnesium of 0.25 - 0.65 % | T6 | EN 1706 | Casting |
Manganese | 0.15 - 0.55 % Show Material materials with Manganese of 0.15 - 0.55 % | T6 | EN 1706 | Casting |
Nickel | 0.2 % Show Material materials with Nickel of 0.2 % | T6 | EN 1706 | Casting |
Silicon | 8.3 - 9.7 % Show Material materials with Silicon of 8.3 - 9.7 % | T6 | EN 1706 | Casting |
Tin | 0.1 % Show Material materials with Tin of 0.1 % | T6 | EN 1706 | Casting |
Titanium | 0.1 - 0.2 % Show Material materials with Titanium of 0.1 - 0.2 % | T6 | EN 1706 | Casting |
Zinc | 0.8 % Show Material materials with Zinc of 0.8 % | T6 | EN 1706 | Casting |
Technological properties
Property | ||
---|---|---|
Anodizing | decorative: not recommended | |
Corrosion properties | general: not sufficient | |
General machinability | after thermal treatment: good, as cast: good | |
Processing methods | permanent mould casting, separately cast test sample |