EN 12844 Grade ZP3

View suppliers (1)
Want to keep this datasheet? Save it now in your required format

Description

The material ZP3 with the material number ZP0400 is applied for pressure castings. If high demands are made on the dimensional accuracy of the pressure casting products, this alloy ought to be preferably used. The material possesses considerably higher ductility than the other alloys. In comparison to the material ZP5 (ZP0410), it shows strength properties that are a little worse as well as lower corrosion-resistance to intercrystalline corrosion. The tensile strength depends on the wall thickness. With the wall thickness of the casting becoming smaller, the strength increases. The casting temperature ought to be about 425 degrees C (450 degrees C maximum) the forming temperature (pressure casting) is to be adjusted to about 180 to 250 degrees C maximum. According to DIN EN 12844, the alternating stress fatigue strength (time strength) is 48 N/mm² with 10 million reversals of stress the creep life (0.5 per cent, 3000 h) is 80 N/mm². The temperature coefficient of the length is 27 µm/m*K.

Related Standards

Equivalent Materials

This material data has been provided by WIAM,AluKey.

"Typical" values were obtained via a literature search. "Predicted" values were imputed via artificial intelligence technology. While we have placed significant efforts in ensuring data accuracy, "typical" and "predicted" data should be considered indicative and verified by appropriate material testing. Please do contact us if additional information on the the predicted data method is required.
All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyTemperatureValue

Density

20.0 °C

6.7 g/cm³

Show Material materials with Density of 6.7 g/cm³

Mechanical

PropertyTemperatureValueComment

Bending Fatigue Strength

23.0 °C

48 MPa

Show Material materials with Bending Fatigue Strength of 48 MPa

Elastic modulus

20.0 °C

85 GPa

Show Material materials with Elastic modulus of 85 GPa

Elongation

20.0 °C

3 %

Show Material materials with Elongation of 3 %

80.0 °C

10 %

Show Material materials with Elongation of 10 %

150.0 °C

21 %

Show Material materials with Elongation of 21 %

Elongation A50

20.0 °C

10 %

Show Material materials with Elongation A50 of 10 %

23.0 °C

10 %

Show Material materials with Elongation A50 of 10 %

Unlock all property charts

Hardness, Brinell

20.0 °C

80 - 83 [-]

Show Material materials with Hardness, Brinell of 80 - 83 [-]

23.0 °C

83 [-]

Show Material materials with Hardness, Brinell of 83 [-]

80.0 °C

55 [-]

Show Material materials with Hardness, Brinell of 55 [-]

150.0 °C

28 [-]

Show Material materials with Hardness, Brinell of 28 [-]

Unlock all property charts

Poisson's ratio

23.0 °C

0.3 [-]

Show Material materials with Poisson's ratio of 0.3 [-]

Typical for Zinc Aluminium

Tensile strength

20.0 °C

275 - 280 MPa

Show Material materials with Tensile strength of 275 - 280 MPa

23.0 °C

280 MPa

Show Material materials with Tensile strength of 280 MPa

80.0 °C

222 MPa

Show Material materials with Tensile strength of 222 MPa

150.0 °C

140 MPa

Show Material materials with Tensile strength of 140 MPa

Unlock all property charts

Yield strength Rp0.2

20.0 °C

200 - 220 MPa

Show Material materials with Yield strength Rp0.2 of 200 - 220 MPa

23.0 °C

200 MPa

Show Material materials with Yield strength Rp0.2 of 200 MPa

80.0 °C

160 MPa

Show Material materials with Yield strength Rp0.2 of 160 MPa

150.0 °C

70 MPa

Show Material materials with Yield strength Rp0.2 of 70 MPa

Unlock all property charts

Thermal

PropertyTemperatureValueComment

Coefficient of thermal expansion

23.0 °C

2.2E-5 - 2.8E-5 1/K

Show Material materials with Coefficient of thermal expansion of 2.2E-5 - 2.8E-5 1/K

Typical for Zinc Aluminium

Melting point

375 - 485 °C

Show Material materials with Melting point of 375 - 485 °C

Typical for Zinc Aluminium

Specific heat capacity

23.0 °C

393 - 525 J/(kg·K)

Show Material materials with Specific heat capacity of 393 - 525 J/(kg·K)

Typical for Zinc Aluminium

Thermal conductivity

20.0 °C

113 W/(m·K)

Show Material materials with Thermal conductivity of 113 W/(m·K)

Electrical

PropertyTemperatureValue

Electrical conductivity

20.0 °C

1.51E+7 S/m

Show Material materials with Electrical conductivity of 1.51E+7 S/m

Electrical resistivity

20.0 °C

6.6E-8 Ω·m

Show Material materials with Electrical resistivity of 6.6E-8 Ω·m

Chemical properties

PropertyValue

Aluminium

3.7 - 4.3 %

Show Material materials with Aluminium of 3.7 - 4.3 %

Cadmium

5E-3 %

Show Material materials with Cadmium of 5E-3 %

Copper

0.1 %

Show Material materials with Copper of 0.1 %

Iron

0.05 %

Show Material materials with Iron of 0.05 %

Lead

5E-3 %

Show Material materials with Lead of 5E-3 %

Magnesium

0.03 - 0.06 %

Show Material materials with Magnesium of 0.03 - 0.06 %

Nickel

0.02 %

Show Material materials with Nickel of 0.02 %

Other

Rest Zn

Silicon

0.03 %

Show Material materials with Silicon of 0.03 %

Tin

2E-3 %

Show Material materials with Tin of 2E-3 %

Zinc

95.43 %

Show Material materials with Zinc of 95.43 %

Looking for suppliers of this material? Click to see 1 supplier of EN 12844 Grade ZP3 on Matmatch