Properties
General
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Density | 2.73 g/cm³ Show Material materials with Density of 2.73 g/cm³ | H22 | AA Standards, ASTM B209 |
Mechanical
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Elastic modulus | 69.0 GPa Show Material materials with Elastic modulus of 69.0 GPa | H22 | AA Standards, ASTM B209 | ||
Elongation A100 | 23.0 °C | 8 % Show Material materials with Elongation A100 of 8 % | |||
Elongation A50 | 23.0 °C | 3 - 9 % Show Material materials with Elongation A50 of 3 - 9 % | |||
Plane-Strain Fracture Toughnes | 22.0 - 35.0 MPa·√m Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m | Typical for Wrought 3000 Series Aluminium | |||
Poisson's ratio | 0.33 [-] Show Material materials with Poisson's ratio of 0.33 [-] | Typical for Wrought 3000 Series Aluminium | |||
Shear modulus | 25.0 - 26.0 GPa Show Material materials with Shear modulus of 25.0 - 26.0 GPa | Typical for Wrought 3000 Series Aluminium | |||
Tensile strength | 120.0 - 160.0 MPa Show Material materials with Tensile strength of 120.0 - 160.0 MPa | H22 | AA Standards, ASTM B209 | ||
Yield strength Rp0.2 | 23.0 °C | 85 MPa Show Material materials with Yield strength Rp0.2 of 85 MPa | |||
Thermal
| Property | Temperature | Value | Condition | Related Standards | Comment |
|---|---|---|---|---|---|
Coefficient of thermal expansion | 100 °C, 20 °C | 2.3199999999999998e-05 1/K Show Material materials with Coefficient of thermal expansion of 2.3199999999999998e-05 1/K | H22 | AA Standards, ASTM B209 | |
Melting point | 640.0 - 655.0 °C Show Material materials with Melting point of 640.0 - 655.0 °C | H22 | AA Standards, ASTM B209 | ||
Specific heat capacity | 893.0 - 920.0 J/(kg·K) Show Material materials with Specific heat capacity of 893.0 - 920.0 J/(kg·K) | Typical for Wrought 3000 Series Aluminium | |||
Thermal conductivity | 159.0 - 193.0 W/(m·K) Show Material materials with Thermal conductivity of 159.0 - 193.0 W/(m·K) | H22 | AA Standards, ASTM B209 | ||
Electrical
| Property | Value | Condition | Related Standards |
|---|---|---|---|
Electrical conductivity | 24000000.0 - 29000000.0 S/m Show Material materials with Electrical conductivity of 24000000.0 - 29000000.0 S/m | H22 | AA Standards, ASTM B209 |
Electrical resistivity | 3.45e-08 - 4.17e-08 Ω·m Show Material materials with Electrical resistivity of 3.45e-08 - 4.17e-08 Ω·m | H22 | AA Standards, ASTM B209 |
Chemical properties
| Property | Value | Condition | Related Standards | ||
|---|---|---|---|---|---|
Copper | 0.05 - 0.2 % Show Material materials with Copper of 0.05 - 0.2 % | H22 | AA Standards, ASTM B209 | ||
Iron | 0.70 % Show Material materials with Iron of 0.70 % | H22 | AA Standards, ASTM B209 | ||
Manganese | 1.0 - 1.5 % Show Material materials with Manganese of 1.0 - 1.5 % | H22 | AA Standards, ASTM B209 | ||
Other | each 0.05, total 0.15, Rest Al | ||||
Silicon | 0.6 % Show Material materials with Silicon of 0.6 % | H22 | AA Standards, ASTM B209 | ||
Zinc | 0.1 % Show Material materials with Zinc of 0.1 % | H22 | AA Standards, ASTM B209 | ||
Technological properties
| Property | ||
|---|---|---|
| Brazing | general: possible with commercial processes and methods | |
| Corrosion properties | Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere | |
| General machinability | General: not suitable (O, H12), poor (H14, H16, H25) | |
| Workability | general (condition): good (O, H12), acceptable (H14, H25), poor(H16, H18) | |