AA Standards Grade 1060 H28

Want to keep this datasheet? Save it now in your required format

Related Standards

Equivalent Materials

This material data has been provided by AluKey.

All metrics apply to room temperature unless otherwise stated. SI units used unless otherwise stated.
Equivalent standards are similar to one or more standards provided by the supplier. Some equivalent standards may be stricter whereas others may be outside the bounds of the original standard.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

Properties

General

PropertyValueConditionRelated Standards

Density

2.705 g/cm³

Show Material materials with Density of 2.705 g/cm³

H28

AA Standards, ASTM B209

Mechanical

PropertyValueConditionRelated StandardsComment

Elastic modulus

69.0 GPa

Show Material materials with Elastic modulus of 69.0 GPa

H28

AA Standards, ASTM B209

Plane-Strain Fracture Toughnes

22.0 - 35.0 MPa·√m

Show Material materials with Plane-Strain Fracture Toughnes of 22.0 - 35.0 MPa·√m

Typical for Wrought 1000 Series Aluminium

Poisson's ratio

0.33 [-]

Show Material materials with Poisson's ratio of 0.33 [-]

Typical for Wrought 1000 Series Aluminium

Shear modulus

25.9 GPa

Show Material materials with Shear modulus of 25.9 GPa

Typical for Wrought 1000 Series Aluminium

Tensile strength

110.0 MPa

Show Material materials with Tensile strength of 110.0 MPa

H28

AA Standards, ASTM B209

Thermal

PropertyTemperatureValueConditionRelated StandardsComment

Coefficient of thermal expansion

100 °C, 20 °C

2.36e-05 1/K

Show Material materials with Coefficient of thermal expansion of 2.36e-05 1/K

H28

AA Standards, ASTM B209

Melting point

645.0 - 655.0 °C

Show Material materials with Melting point of 645.0 - 655.0 °C

H28

AA Standards, ASTM B209

Specific heat capacity

900.0 - 963.0 J/(kg·K)

Show Material materials with Specific heat capacity of 900.0 - 963.0 J/(kg·K)

Typical for Wrought 1000 Series Aluminium

Thermal conductivity

230.0 - 234.0 W/(m·K)

Show Material materials with Thermal conductivity of 230.0 - 234.0 W/(m·K)

H28

AA Standards, ASTM B209

Electrical

PropertyValueConditionRelated Standards

Electrical conductivity

35000000.0 - 36000000.0 S/m

Show Material materials with Electrical conductivity of 35000000.0 - 36000000.0 S/m

H28

AA Standards, ASTM B209

Electrical resistivity

2.78e-08 - 2.86e-08 Ω·m

Show Material materials with Electrical resistivity of 2.78e-08 - 2.86e-08 Ω·m

H28

AA Standards, ASTM B209

Chemical properties

PropertyValueConditionRelated Standards

Aluminium

99.6 %

Show Material materials with Aluminium of 99.6 %

H28

AA Standards, ASTM B209

Copper

0.05 %

Show Material materials with Copper of 0.05 %

H28

AA Standards, ASTM B209

Iron

0.35 %

Show Material materials with Iron of 0.35 %

H28

AA Standards, ASTM B209

Magnesium

0.03 %

Show Material materials with Magnesium of 0.03 %

H28

AA Standards, ASTM B209

Manganese

0.03 %

Show Material materials with Manganese of 0.03 %

H28

AA Standards, ASTM B209

Silicon

0.25 %

Show Material materials with Silicon of 0.25 %

H28

AA Standards, ASTM B209

Titanium

0.03 %

Show Material materials with Titanium of 0.03 %

H28

AA Standards, ASTM B209

Vanadium

0.05 %

Show Material materials with Vanadium of 0.05 %

H28

AA Standards, ASTM B209

Zinc

0.05 %

Show Material materials with Zinc of 0.05 %

H28

AA Standards, ASTM B209

Technological properties

Property
Brazing

general: possible with commercial processes and methods

Corrosion properties

Stress corrosion cracking: no damage during operation and laboratory tests, general: very good, without protection in industrial or seawater atmosphere

General machinability

General: not suitable (O, H12), poor (H14, H16, H18)

Workability

general (condition): good (O, H12, H14), acceptable (H16, H18)