Properties
General
| Property | Temperature | Value |
|---|---|---|
Density | 23.0 °C | 7.53 g/cm³ Show Supplier Material materials with Density of 7.53 g/cm³ |
Recycled Content | 80 % Show Supplier Material materials with Recycled Content of 80 % |
Mechanical
| Property | Temperature | Value | Comment |
|---|---|---|---|
Charpy impact energy | 23.0 °C | 11.3 J Show Supplier Material materials with Charpy impact energy of 11.3 J | |
Compressive strength | 23.0 °C | 965 - 1034 MPa Show Supplier Material materials with Compressive strength of 965 - 1034 MPa | |
Compressive yield strength, 0.1% | 23.0 °C | 303 MPa Show Supplier Material materials with Compressive yield strength, 0.1% of 303 MPa | |
Elastic modulus | 23.0 °C | 117 GPa Show Supplier Material materials with Elastic modulus of 117 GPa | |
Elongation A5 | 23.0 °C | 15 - 20 % Show Supplier Material materials with Elongation A5 of 15 - 20 % | |
Fatigue strength | 23.0 °C | 255 - 262 MPa Show Supplier Material materials with Fatigue strength of 255 - 262 MPa | 100.000.000 cycles |
Hardness, HBW | 23.0 °C | 212 - 228 [-] Show Supplier Material materials with Hardness, HBW of 212 - 228 [-] | HBW 10/3000 |
Hardness, Rockwell B | 23.0 °C | 96 - 98 [-] Show Supplier Material materials with Hardness, Rockwell B of 96 - 98 [-] | |
Izod impact energy | 23.0 °C | 13.6 J Show Supplier Material materials with Izod impact energy of 13.6 J | |
Proportional limit in compression | 23.0 °C | 262 - 276 MPa Show Supplier Material materials with Proportional limit in compression of 262 - 276 MPa | |
Reduction of area | 23.0 °C | 15 - 20 % Show Supplier Material materials with Reduction of area of 15 - 20 % | |
Shear strength | 23.0 °C | 448 - 483 MPa Show Supplier Material materials with Shear strength of 448 - 483 MPa | |
Tensile strength | 23.0 °C | 772 - 814 MPa Show Supplier Material materials with Tensile strength of 772 - 814 MPa | |
Yield strength Rp0.5 | 23.0 °C | 420 - 517 MPa Show Supplier Material materials with Yield strength Rp0.5 of 420 - 517 MPa |
Thermal
| Property | Temperature | Value |
|---|---|---|
Coefficient of thermal expansion | 23.0 °C | 1.62E-5 1/K Show Supplier Material materials with Coefficient of thermal expansion of 1.62E-5 1/K |
Specific heat capacity | 23.0 °C | 450 J/(kg·K) Show Supplier Material materials with Specific heat capacity of 450 J/(kg·K) |
Thermal conductivity | 23.0 °C | 46 W/(m·K) Show Supplier Material materials with Thermal conductivity of 46 W/(m·K) |
Electrical
| Property | Temperature | Value |
|---|---|---|
Electrical conductivity | 23.0 °C | 5.00E+6 S/m Show Supplier Material materials with Electrical conductivity of 5.00E+6 S/m |
Specific Electrical conductivity | 9 % IACS Show Supplier Material materials with Specific Electrical conductivity of 9 % IACS |
Chemical properties
| Property | Value |
|---|---|
Aluminium | 10 % Show Supplier Material materials with Aluminium of 10 % |
Copper | Balance |
Iron | 2.5 % Show Supplier Material materials with Iron of 2.5 % |
Manganese | 1 % Show Supplier Material materials with Manganese of 1 % |
Nickel | 5 % Show Supplier Material materials with Nickel of 5 % |
Other | 0.5 % Show Supplier Material materials with Other of 0.5 % |
Technological properties
| Property | ||
|---|---|---|
| Application areas | AMPCO® 45 is recommended for heavy-duty high-loaded mechanical and corrosive applications. Typical applications involving abrasive wear, friction, deformation, chemical erosion include: Aircraft bearings/bushings, Pump, marine shafts and wear rings, Valve spindles and seats, Machine tool parts. The spark-resistance properties make it suitable for safety tools and machine tool components in explosive environments. | |